Rapid Synthesis of Polymer-Grafted Cellulose Nanofiber Nanocomposite Via Surface-Initiated Cu(0)-Mediated Reversible Deactivation Radical Polymerization

Sikai Chen,Ze-Lian Zhang,Fei Song,Xiu-Li Wang,Yu-Zhong Wang

DOI: https://doi.org/10.1021/acs.macromol.1c00903

IF: 5.5

2021-01-01

Macromolecules

Abstract:Facing the limitation of weak compatibility on the use of cellulose nanofiber (CNF) as a reinforcement in polymer matrix nanocomposites, this work developed an alternative approach to fabricating a series of one-component CNF-reinforced nanocomposites by grafting polyacrylates from CNF via surface-initiated Cu(0)-mediated reversible deactivation radical polymerizations. An initiator group was initially introduced onto the surface of CNF through one-step esterification. Then, graft polymerization of methyl acrylate and n-butyl acrylate was carried out to obtain polyacrylate-grafted CNF. The graft polymerization exhibited several advantages, including simplicity, rapidity, and effectivity. A high graft ratio (up to 3000%) was obtained at room temperature after 3 h. The graft ratio was controlled by regulating the monomer concentration and reaction time. Characterizations confirmed that the chemical, morphological, and crystalline structure of CNF was maintained after surface modification and grafting. The uniform morphology and moderated transparency of solvent-casting polyacrylate-grafted CNF films proved the superior homogeneity of these nanocomposites. Tensile experiments revealed that poly(methyl acrylate)-grafted CNF nanocomposites had remarkable mechanical properties (tensile strength = 13.6-25.3 MPa; break elongation = 48.8-179.9%), contributing to an outstanding dispersity. By alternating the graft ratio, the mechanical behavior of the nanocomposite could transition from tough to ductile. This grafting approach has been proven to be a powerful tool for the design of CNF-reinforced nanocomposites for various purposes.