Modified Diatomite-Based Porous Ceramic To Develop Shape-Stabilized Nano3 Salt With Enhanced Thermal Conductivity For Thermal Energy Storage

Feng Jiang,Xiang Ling,Lingling Zhang,Daqiang Cang,Yulong Ding

DOI: https://doi.org/10.1016/j.solmat.2021.111328

IF: 6.9

2021-01-01

Solar Energy Materials and Solar Cells

Abstract:Low thermal conductivity and corrosion problem of NaNO3 salt-based phase change materials (PCMs) are regarded as two critical barriers for their applications in thermal energy storage. To address the above problem, a diatomite-based porous ceramic modified by CaCO3 was firstly used to develop shape-stabilized NaNO3 in this work. Particularly, contribution of modified diatomite-based ceramic on improving thermal conductivity of the composite was investigated. Compared with traditional diatomite-based skeleton, diatomite-based ceramic was found to contribute to a 129% higher thermal conductivity of composites, benefited by the generation of a dense and continuous skeleton that consisted of newly formed cristobalite phase with a higher thermal conductivity. While crack occurred on the composite with diatomite-based ceramic after 100 thermal cycles, resulting in the leakage of salt and the decrease of thermal conductivity. By contrast, diatomite-based ceramic modified by no more than 40 wt% CaCO3 effectively avoided the crack of composites, exhibiting quite a stability in shape and thermal conductivity during 500 thermal cycles. The modified ceramic was shown to improve the thermal conductivity of loaded NaNO3 by 118%, up to 1.22 W/(m.K) at 25 degrees C. The results also indicated that the modified ceramic hardly changed the phase transition temperature of NaNO3, but decreased the latent heat of composites, while possessed a much higher capacity to load salt (57 wt% NaNO3) than that of other porous ceramics. The composite with modified ceramic was demonstrated to have a good cycling stability in thermal properties as well, which performed a considerable potential in thermal energy storage.