Creep Damage Repair of a Nickel-Based Single Crystal Superalloy Based on Heat Treatment

Xiaoyan Wang,Meng Li,Yuansheng Wang,Chengjiang Zhang,Zhixun Wen

DOI: https://doi.org/10.3390/met11040623

IF: 2.695

2021-01-01

Metals

Abstract:Taking nickel-based single crystal superalloy DD6 as the research object, different degrees of creep damage were prefabricated by creep interruption tests, and then the creep damage was repaired by the restoration heat treatment system of solid solution heat treatment and two-stage aging heat treatment. The results show that with the creep time increasing, the alloy underwent microstructure evolution including gamma ' phase coarsening, N-type rafting and de-rafting. After the restoration heat treatment, the coarse rafted gamma ' phase of creep damaged specimens dissolved, precipitated, grew up, and became cubic again. Except for the specimens with creep interruption of 100 h, the gamma ' phase can basically achieve the same arrangement as the gamma ' phase of the original sample. The comparison of the secondary creep test shows that the steady-state creep stage of the test piece after the restoration heat treatment is relatively increased, and the total creep life can reach the same level as the primary creep life. The high temperature creep properties of the tested alloy are basically recovered, and the restoration heat treatment effect is good.