Arsenic removal from acid extraction solutions of copper smelting flue dust
Guangya Zheng,Jupei Xia,Hailang Liu,Zhengjie Chen
DOI: https://doi.org/10.1016/j.jclepro.2020.125384
IF: 11.1
2021-02-01
Journal of Cleaner Production
Abstract:<p>Multi-metal extraction of flue dust from copper smelting is being pursued to meet the increasingly appealing environmental requirements of our modern life. In this paper, the thermodynamic analysis of acid leaching solution was carried out. Ferric arsenate deposits were found in the range of pH = 0∼11.63, in the form of FeAsO<sub>4</sub> and FeAsO<sub>4</sub>∙2H<sub>2</sub>O. Cu<sub>2</sub>AsO<sub>4</sub>OH, CuHAsO<sub>4</sub>, and Cu<sub>5</sub>H<sub>2</sub>(AsO<sub>4</sub>)<sub>4</sub> forms of Cu<sub>2</sub>AsO<sub>4</sub> were produced in the range of pH = 0.98∼2.33. Zn<sub>3</sub>(AsO<sub>4</sub>)<sub>2</sub>, Zn<sub>2</sub>AsO<sub>4</sub>OH, ZnHAsO<sub>4</sub>, and Zn<sub>5</sub>H<sub>2</sub>(AsO<sub>4</sub>)<sub>4</sub> forms of zinc arsenate were produced in the range of pH = 1.40∼4.85. Theoretically, when pH = 0.98∼2.33, copper arsenate salt was produced; however, when the actual experimental results were at pH ≥ 1.2, a small amount of copper co-settling occurred. Theoretical results were verified by single factor experiments. Strictly controlling the pH value of the reaction system can effectively separate arsenic (As) from copper (Cu) and zinc (Zn). Through single factor experimentation, optimal process parameters of iron salt and calcium salt combined with As removal were as follows: reaction time, 5 h; reaction temperature, 85 °C; pH value, 1.2; Fe-As molar ratio, 1.5; no H<sub>2</sub>O<sub>2</sub> added. Under these conditions, the precipitation rate of As was 89.12%, while Cu and Zn did not precipitate. Through XRD analysis, As element was removed from acid leaching solution in the form of scorodite (FeAsO<sub>4</sub>∙2H<sub>2</sub>O). This has laid a theoretical foundation for the effective removal of As in acid leaching solution and the reduction of As content.</p>
environmental sciences,green & sustainable science & technology,engineering, environmental