Hierarchical Ni2P@Ni(OH)2 Architectures Supported on Carbon Cloth As Battery-Type Electrodes for Hybrid Supercapacitors with Boosting Specific Capacitance and Cycle Stability

Yingying Lan,Hongna Xing,Yan Zong,Yong Sun,Linxue Zhang,Yajing Wang,Xinghua Li,Xinliang Zheng

DOI: https://doi.org/10.1007/s10854-021-05521-5

2021-01-01

Journal of Materials Science Materials in Electronics

Abstract:In this work, a novel binder-free electrode, in which three-dimensional porous Ni 2 P@Ni(OH) 2 nanosheet arrays were in-situ grown on carbon cloth (CC), is rationally designed for supercapacitor applications. In comparison with Ni 2 P@CC, the Ni 2 P@Ni(OH) 2 @CC electrode represents superior electrochemical characteristics: the gravimetric capacitance and areal capacitance are boosted to be 632 C g -1 and 0.73 C cm -2 at 1 mA cm -2 , about 2 and 2.7 times larger than those of Ni 2 P@CC (321 C g -1 and 0.27 C cm -2 ), respectively; the rate capability is improved to be 63.3% from 1 to 10 mA cm -2 , about 1.5 times larger than Ni 2 P@CC (42.9%); the cycle stability is enhanced to be 81.4% after 1000 cycles, about 1.6 times larger than Ni 2 P/CC (51.8%). The assembly Ni 2 P@Ni(OH) 2 @CC//AC hybrid supercapacitor device shows high energy density of 23.5 Wh kg -1 at a power density of 1158.0 W kg -1 and good cycling stability of 75.2% maintenance after 5000 cycles. Benefiting from the combined advantages of high electronic conductivity and large specific capacitance of Ni 2 P, superior anion exchanging/intercalating capacity of Ni(OH) 2 , excellent flexibility of carbon cloth and special hierarchical architecture with large surface area, the Ni 2 P@Ni(OH) 2 @CC electrode is promised to be a good candidate for supercapacitors.