Abstract:The addition of microencapsulated phase-change materials (MPCM) to concrete will inevitably cause changes in the mechanical and thermal properties of concrete, and this is vitally important for the safety and energy saving of concrete building components. In this research, shale ceramsite and shale ceramics sand were used as the main raw materials to produce lightweight aggregate concrete (LWAC) mixed with MPCM. In order to investigate the effect of MPCM content and phase-change cycle numbers on the mechanical and thermal properties of MPCM-LWAC, two groups of MPCM-LWAC specimens were prepared. One group consists of specimens containing 2.5%, 5.0%, 7.5%, and 10% MPCM, respectively, and they are used to reveal the change law of tensile strength, compressive strength, enthalpy, and specific heat capacity of LWAC integrated into MPCM. The other group includes specimens with the same MPCM content, but the specimens are subjected to different phase-change cycle numbers of 50, 100, 150, and 200 at the environment temperature of −10–60°C to study the thermal properties of MPCM-LWAC. Findings from the experimental results include the following: (1)The tensile and compressive strengths of MPCM-LWAC concrete are negatively correlated with the MPCM content, while the enthalpy and specific heat capacity are positively correlated with the MPCM content. When the MPCM content reaches 10%, the compressive and tensile strengths of MPCM-LWAC decreased, respectively, by 45.49% and 52.63% than the LWAC without MPCM. (2) Under heating and curing condition, the corresponding maximum specific heat capacity of LWAC with 10% MPCM is 328.35% and 249.50% higher than the LWAC without MPCM, respectively, and the average specific heat capacities increase 71.21% and 44.94%, respectively. (3) The melting enthalpy of MPCM-LWAC is slightly larger than the curing enthalpy, and the difference is more noticeable with the increase of MPCM content. In addition, when the number of phase-change cycle is below 200, the compressive strength and splitting tensile strength of MPCM-LWAC decrease by less than 5%, and the specific heat capacity decreases by less than 1.33%. Hence, it concludes that shale ceramsite concrete with MPCM has promising application prospects.

Mechanical and Microstructure Development of Portland Cement Modified with Micro-Encapsulated Phase Change Materials

Research on the modification of microencapsulated phase change material for thermal energy storage by nano-SiO2 and graphite

Thermophysical and Mechanical Properties of Hardened Cement Paste with Microencapsulated Phase Change Materials for Energy Storage

The thermal performances of cement-based materials with different types of microencapsulated phase change materials

Understanding the compressive strength degradation mechanism of cement-paste incorporating phase change material

Enhanced thermo-mechanical properties of cementitious composites via red mud-based microencapsulated phase change material: Towards energy conservation in building

Experimental and Numerical Investigations on the Inhibition of Freeze–thaw Damage of Cement-Based Materials by a Methyl Laurate/diatomite Microcapsule Phase Change Material

Thermal and Mechanical Properties of Ultra-High Performance Concrete Incorporated with Microencapsulated Phase Change Material

Enabling thermal energy storage in structural cementitious composites with a novel phase change material microcapsule featuring an inorganic shell and a bio-inspired silica coating

Mechanical and Thermal Properties of Shale Ceramsite Concrete: Experimental Study on the Influence Law due to Microencapsulated Phase-Change Material Content and Phase-Change Cycle Numbers

Microstructure and Mechanical Properties of Phase Change Cloud Concrete Stone Cementitious Composites

A Novel Thermal-Tailored Strategy to Mitigate Thermal Cracking of Cement-Based Materials by Carbon Fibers and Liquid-Metal-based Microencapsulated Phase Change Materials

A Robust, Compatible, and Effective Core-Shell Structured Phase Change Materials for Controlling the Temperature Rise Caused by Cement Hydration

Enhance the thermal storage of cement-based composites with phase change materials and carbon nanotubes

Experimental Research on Thermomechanical Properties of Thermal Energy Storage Cement Mortar Incorporated with Phase-Change Material

Thermal, mechanical and microstructural analysis of concrete containing microencapsulated phase change materials

Thermal and Mechanical Properties of Thermal Energy Storage Lightweight Aggregate Mortar Incorporated with Phase Change Material

Thermo-mechanical properties of compaction molded cement-based composite containing a high mass fraction of phase change material for thermal energy storage

Encapsulated Phase Change Material on Performance of Cement Mortar at Varied Temperature

Preparation and Characterizations of Hydroxyapatite Microcapsule Phase Change Materials for Potential Building Materials

Thermal stability and mechanical properties of epoxy resin/microcapsule composite phase change materials