Abstract:Tungstovanadophosphoric heteropoly acid H6PW9V3O40 center dot(13.81 +/- 0.13)H2O (abbreviated as PW9V3) has been synthesized by the stepwise acidification and the stepwise addition of element solutions. The crystal structure was determined from single crystal X-ray diffraction. The complex crystallizes in the space group R (3) over barm, with a = 16.4374 (9) angstrom, b = 16.4374 (9) angstrom, c = 25.3866 (14) angstrom, alpha = 90, beta = 90 degrees, gamma = 120, V = 5940.20 angstrom, and Z = 6. The product possesses Keggin structure, and its conductivity was 1.730 x 10(-2) S.cm(-1) at 26 degrees C and 75% relative humidity by electrochemical impedance spectroscopy (EIS) measurement. Two conducting systems were prepared with a mixture of as-synthesized PW9V3 and organic polymers [polyvinylpyrrolidone (PVP) or polyethylene glycol (PEG)] at the weight ratio 80:20. The hybrid materials exhibit high proton conductivities with 7.110 x 10(-3) and 1.050 x 10(-2) S.cm(-1) (PW9V3/PEG) at 26 degrees C and 75% relative humidity, respectively. Their activation energies of proton conduction are 15.23 and 13.67 kJ.mol(-1), which are lower than that of pristine heteropoly acid (25.68 kJ.mol(-1)). Their mechanisms of proton conduction are also proposed.

A Typical Solid High-Protonic Conductor: A Kind of Vanadium-Substituted Heteropoly Acid H5PW10V2O40·15H2O

Synthesis and High Proton Conductive Performance of Vanadium-Substituted Dawson Structure Heteropoly Acid H8P2W16V2O62·20H2O

Synthesis and conduction mechanism of high proton conductor H6SiW10V2O40⋅14H2O

Synthesis and Structure of a Proton-Conductive Supramolecular Complex Based on Poly-Keggin-anion Chains

Synthesis and Conductive Performance about a Kind of High-Proton Conductor, Dawson Structure Heteropoly Acid H6P2W16Mo2O40 ⋅ 29H2O

Synthesis And Conductivity Of Solid High-Proton Conductor H5gew10movo40 Center Dot 21h(2)O

Solid High-Proton Conductor Tungstovanadozincic Acid with Transition Metal As Central Atom: Synthesis and Conductivity

Synthesis and conductivity of solid high-proton conductor H5GeW10MoVO40·21H2O

A Stable Nh4po3-Glass Proton Conductor for Intermediate Temperature Fuel Cells

Synthesis and Conductivity of Heptadecatungstovanadodiphosphoric Heteropoly Acid with Dawson Structure

Synthesis and high proton conductive performance of a quaternary vanadomolybdotungstosilicic heteropoly acid.

Synthesis and Performance of Solid Proton Conductor Molybdovanadosilicic Acid

Synthesis and Conductive Performance of Quaternary Heteropoly Acid H5SiW9Mo2VO40⋅13H2O

Synthesis and Electrochemical Properties of Substituted Heteropoly Acid with Dawson Structure H7[In(H2O)P2W17O61]·23H2O.

Synthesis and conductivity of substituted heteropoly acid with Dawson structure H 7 [Ga(H 2 O)P 2 W 17 O 61 ]·18H 2 O

Synthesis and conductive performance of quaternary heteropoly acid H5SiW9Mo2VO40 center dot 13H(2)O

Preparation and performance of solid high-proton conductor ternary undecatungstocobaltoaluminic heteropoly acid

Preparation and Conductivity Study of Hybrid High Proton Conductor Materials Composited with Octadecatungstodiphosphoric Heteropoly Acid with Dawson Structure

Preparation and Electrochemical Performance of Tungstovanadophosphoric Heteropoly Acid and Its Hybrid Materials

Solid High-Proton Conductors Based on Heteropoly Acids

Synthesis and conductive performance of quaternary molybdotungstovanadophosphoric heteropoly acid with Keggin structure