Improved ferroelectric properties in hybrid improper ferroelectric Sr_3-<i>x</i>Ba<i>_x</i>Zr₂O₇

Z. Z. Hu,J. J. Lu,B. H. Chen,X. Q. Liu,X. M. Chen

DOI: https://doi.org/10.1016/j.jallcom.2021.158705

IF: 6.2

2021-01-01

Journal of Alloys and Compounds

Abstract:In the present work, Sr3-xBaxZr2O7 (x = 0.1, 0.2, 0.3) ceramics with Ruddlesden-Popper structures were prepared by a standard solid-state reaction method. The refinement results showed that the present ceramics formed a single orthorhombic phase with A2(1)am space groups. The lattice constant and tolerance factor increased while the Curie temperature decreased linearly with increasing the content of barium cations, and the typical first-order improper ferroelectric phase transitions were determined in all ceramics. Moreover, the declines of oxygen octahedral rotation angle and coercive field were observed, while the enhanced remanent polarizations were found, therefore the improved ferroelectric properties were achieved by introducing the barium cations. The sharper decline of Curie temperature was induced by the hetero-valent substitution in contrast to the universal relationship between Curie temperature and tolerance factor. From the present work, the tolerance factor could not determine ferroelectric properties, and the possible way to improve ferroelectric properties was explored for Sr3Zr2O7-based ceramics. (C) 2021 Elsevier B.V. All rights reserved.