Dynamic mechanical behaviour of three-dimensional random fibrous materials at high temperatures

Datao Li,Jinsong Jiang,Chao Zhang,Wenshan Yu,Pengmin Lu,Shengping Shen
DOI: https://doi.org/10.1016/j.compstruct.2021.114593
IF: 6.3
2021-01-01
Composite Structures
Abstract:We studied the dynamic mechanical behaviour of three-dimensional (3D) random fibrous (RF) materials at various strain rates using a high-temperature split Hopkinson pressure bar (SHPB) system from 288 to 1423 K. The failure mode of 3D RF materials in the in-plane (IP) direction exhibits a shear fracture mode with an angle of ~30° at a strain rate of 300/s, and the bonding between fibres remains intact at 288 K despite the fracture in fibres. The variation of dynamic strength at a strain rate of 500/s (from 288 to 773 K, the strength increases from 4.72 ± 0.61 to 5.27 ± 1.03 MPa; from 773 to 1423 K, the strength decreases from 5.27 ± 1.03 to 3.36 ± 0.93 MPa) aligned well with observations of the static experiment with increasing temperature. We determined the strain rate sensitivity factor by fitting strength versus strain rate at various temperatures and observed a significant effect of the strain rate sensitivity on strength at 288, 773, and 1273 K. However, the effect of strain rate on the strength is low at the transition temperature of viscous flow and brittle deformation of 3D RF materials. These results can be used as the theoretical basis for the preparation and performance evaluation of 3D RF materials.
What problem does this paper attempt to address?