In Situ Observation of Sodium Dendrite Growth and Concurrent Mechanical Property Measurements Using an Environmental Transmission Electron Microscopy–Atomic Force Microscopy (ETEM-AFM) Platform
Qiunan Liu,Liqiang Zhang,Haiming Sun,Lin Geng,Yanshuai Li,Yushu Tang,Peng Jia,Zaifa Wang,Qiushi Dai,Tongde Shen,Yongfu Tang,Ting Zhu,Jianyu Huang
DOI: https://doi.org/10.1021/acsenergylett.0c01214
IF: 22
2020-07-07
ACS Energy Letters
Abstract:Akin to Li, Na deposits in a dendritic form to cause a short circuit in Na metal batteries. However, the growth mechanisms and related mechanical properties of Na dendrites remain largely unknown. Here we report real-time characterizations of Na dendrite growth with concurrent mechanical property measurements using an environmental transmission electron microscopy–atomic force microscopy (ETEM-AFM) platform. <i>In situ</i> electrochemical plating produces Na deposits stabilized with a thin Na<sub>2</sub>CO<sub>3</sub> surface layer (referred to as Na dendrites). These Na dendrites have characteristic dimensions of a few hundred nanometers and exhibit different morphologies, including nanorods, polyhedral nanocrystals, and nanospheres. <i>In situ</i> mechanical measurements show that the compressive and tensile strengths of Na dendrites with a Na<sub>2</sub>CO<sub>3</sub> surface layer vary from 36 to >203 MPa, which are much larger than those of bulk Na. <i>In situ</i> growth of Na dendrites under the combined overpotential and mechanical confinement can generate high stress in these Na deposits. These results provide new baseline data on the electrochemical and mechanical behavior of Na dendrites, which have implications for the development of Na metal batteries toward practical energy-storage applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsenergylett.0c01214?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsenergylett.0c01214</a>.Supplementary Methods. <i>In situ</i> ETEM-AFM, synthesis of arc-discharged CNTs, effects of surface Na<sub>2</sub>CO<sub>3</sub> layer on the mechanical properties of Na dendrites, molar volume calculation of Li and Na, and quantification of bending off the image plane. Figure S1. Na substrate covered by a Na<sub>2</sub>CO<sub>3</sub> SEI layer with a thickness of 110–140 nm and Na nanospheres grown on the Na substrate. Low-loss and a core-loss EELS of the Na substrate. Figure S2. Growth thickness of the Na<sub>2</sub>CO<sub>3</sub> layer versus time for four typical Na dendrites. Figure S3. <i>In situ</i> TEM images of the Na dendrite growth. Current flowing in the dendrite. Figure S4. Time-lapse TEM images showing the growth of a Na nanorod via electrochemical plating. EDP of the Na dendrite. Dark-field image of the Na dendrite formed by selecting the (110) reflections in the EDP. Low-loss and core-loss EELS showing the characteristics of Na. Figure S5. Time-lapse TEM images showing the growth of a Na nanocube via electrochemical plating. EDP of the Na nanocube. The nanocube appears to be heavily strained, suggesting there exists significant diffusion induced stress during the growth. Figure S6. Na dendrite was exposed to ebeam irradiation for 887 s in a CO<sub>2</sub> ambient, showing no discernible irradiation damage due to the protection of the surface Na<sub>2</sub>CO<sub>3</sub> layer. Under no gas condition, the dendrite only grew with a Na plate. Figure S7. Sequential TEM images showing the compression process and the corresponding force-displacement of a Na nanorod. Figure S8. Two sets of <i>in situ</i> compression tests of as-grown Na dendrites. Figure S9. Three sets of <i>in situ</i> tensile tests of as-grown Na dendrites. Figure S10. Tilting the as-grown Na dendrite from −14.8 to 27.2°. Figure S11. Tilting the as-grown Na dendrite from −12.9 to 29.4°. Figure S12. Tilting the as-grown Na nanorod from 3.1 to −28.6°. Table S1. Mechanical data corresponding to <a class="internalNav" href="#fig4">Figure </a><a class="internalNav" href="#fig4">4</a>. Table S2. Mechanical data corresponding to <a class="ext-link" href="/doi/suppl/10.1021/acsenergylett.0c01214/suppl_file/nz0c01214_si_001.pdf">Figure S7</a>. Table S3. Mechanical data corresponding to <a class="internalNav" href="#fig5">Figure </a><a class="internalNav" href="#fig5">5</a>. References (<a class="ext-link" href="/doi/suppl/10.1021/acsenergylett.0c01214/suppl_file/nz0c01214_si_001.pdf">PDF</a>)Movie S1. <i>In situ</i> TEM movie showing the growth of a Na dendrite (<a class="internalNav" href="#fig1">Figure </a><a class="internalNav" href="#fig1">1</a>) (<a class="ext-link" href="/doi/suppl/10.1021/acsenergylett.0c01214/suppl_file/nz0c01214_si_002.avi">AVI</a>)Movie S2. <i>In situ</i> TEM movie showing the growth of a Na dendrite (<a class="internalNav" href="#fig2">Figure </a><a class="internalNav" href="#fig2">2</a>a–e) (<a class="ext-link" href="/doi/suppl/10.1021/acsenergylett.0c01214/suppl_file/nz0c01214_si_003.avi">AVI</a>)Movie S3. <i>In situ</i> TEM movie showing the growth of a Na dendrite under different potentials (<a class="internalNav" href="#fig2">Figure </a><a class="internalNav" href="#fig2">2</a>m–s) (<a class="ext-link" href="/doi/suppl/10.1021/acsenergylett.0c01214/suppl_file/nz0c01214_si_004.avi">AVI</a>)Movie S4. <i>In situ</i> TEM movie showing the growth of a N <p>-Abstract Truncated-</p>
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology,energy & fuels,electrochemistry