Bi₄O₅I₂-Bi₅O₇I/Ni foam constructed in-situ accelerating interfacial carrier transfer for efficient photocatalysis

Shaomang Wang,Wen An,Yuan Guan,Zhongyu Li,Danjun Mao,Tao Xu,Haoran Wang,Zhihao Hu,Shicheng Yan

DOI: https://doi.org/10.1016/j.apsusc.2021.150485

IF: 6.7

2021-01-01

Applied Surface Science

Abstract:BiOI powder was first supported on Ni foam to form BiOI/Ni foam. The Bi4O5I2-Bi5O7I/Ni foam was obtained by calcining the BiOI/Ni foam at 400 degrees C for 1 h with a ramp rate of 10 degrees C min(-1), which demonstrated excellent photocatalytic performance in the removal of RhB from water. Approximately 99% of RhB was decomposed over Bi4O5I2-Bi5O7I/Ni foam under irradiation of a 500 W xenon lamp for 5 h, 41% higher than that over BiOI powder calcined under the same conditions. The removal rates of total organic carbon and total organic nitrogen were about 47% and 38%, respectively. Degradation rate of RhB only decreased by 2% after the Bi4O5I2-Bi5O7I/Ni foam was used for 5 rounds. Photo-induced electrons flowed from Bi4O5I2 to Bi5O7I, to Ni foam, while photogenerated holes migrated in the reverse direction. The rapid migration of photo-induced electrons and holes on the interface of Bi4O5I2-Bi5O7I/Ni foam oppositely enhanced its photocatalytic activity for better degradation of RhB.