Abstract:We synthesized a self-healing polyurethane elastomer (PU-SSDA) which displayed excellent healing efficiency at room temperature due to the synergistic contribution of dynamic covalent D-A bond and S-S bond. Mechanical and self-healing properties of the polyurethane elastomers were characterized by tensile test and three-dimensional super depth of field microscope. The cross-linking structure of PU-SSDA is explored by extraction experiments, demonstrating that there are not only crosslinked structures but also linear molecular segments existed in the polyurethane elastomer. Mechanical properties of the PU-SSDA elastomer can be tuned by changing the cross-linking degree. As the crosslinking degree increases from 25% to 45%, the tensile strength increases from 2.9 MPa to 5.5 MPa while the elongation at break decreases from 795% to 304%. After optimization, when the crosslinking degree was 35%, the tensile strength was 3.7 MPa, the elongation at break was 606% and the repair efficiency could be restored to 93% after healing for 60 min at room temperature. Moreover, the healing efficiency still remains above 90% after 4 damage-healing cycles. In addition, the PU-SSDA elastomer can also be reprocessed by hot pressing at 120 degrees C. This excellent self-healing behavior and reprocessable property were attributed to the reversible fracture recombination reaction of dynamic D-A and S-S bonds and the quick infiltration of the linear polymer chains into damaged surface. The self-healing mechanism can be further confirmed by the dissolution experiments which showed that the PU-SSDA elastomer can be dissolved in DMF at 100 degrees C while the PU-control can only swell under the same conditions, demonstrating that the reversible cleavage and reformation of D-A and S-S bonds contribute a lot to the self-healing process. Due to the facile and friendly preparation method, fast self-healing behavior at room temperature and fully reprocessable properties, the as prepared polyurethane elastomers displayed wide potential applications such as protection coatings and wearable electronic devices.

Self-healing and reprocessing of transparent UV-cured polysiloxane elastomer

Self-healing, Reprocessing and 3D Printing of Transparent and Hydrolysis-Resistant Silicone Elastomers

Designed Preparation of Silicone Protective Materials with Controlled Self-Healing and Toughness Properties

Facile Preparation of a Transparent, Self-Healing, and Recyclable Polysiloxane Elastomer Based on a Dynamic Imine and Boroxine Bond

Design of Robust Self-Healing Silicone Elastomers Based on Multiple H-Bonding and Dynamic Covalent Bond

Self‐Healable and Transparent Elastomers Based on Dual Reversible Networks

Self-healable, Recyclable, Mechanically Tough Transparent Polysiloxane Elastomers Based on Dynamic Microphase Separation for Flexible Sensor

Self-Healing Polysiloxane Elastomer Based on Integration of Covalent and Reversible Networks

Heat-Triggered Poly(Siloxane-Urethane)S Based On Disulfide Bonds For Self-Healing Application

Healable and Reprocessable Silica/poly(oxime‐urethane) Composite Elastomer with High Mechanical Robustness and Exceptional Damage‐tolerant Capacity

A Self-Healing Polydimethylsiloxane Elastomer with High Strength and High Modulus

Robust, Self-Healable Siloxane Elastomers Constructed by Multiple Dynamic Bonds for Stretchable Electronics and Microsystems

Room-temperature self-healing polysiloxane elastomer with reversible cross-linked network

A self-healing, re-moldable and biocompatible crosslinked polysiloxane elastomer

A Transparent, Highly Stretchable, Autonomous Self-Healing Poly(dimethyl siloxane) Elastomer

Preparation of highly transparent, room-temperature self-healing and recyclable silicon elastomers based on dynamic imine bond and their ion responsive properties

A Self-Healing Polysiloxane Elastomer Based on Siloxane Equilibration Synthesized Through Amino-Ene Michael Addition Reaction

A High Strength, High Toughness and Transparent Room-Temperature Self-Healing Elastomer Based on the Synergy Effect of Quadruple Dynamic Bonding Structure

Preparation and Properties of Multiple Dynamic Crosslinked Poly(siloxane‐urethane)

Preparation of Robust, Room-Temperature Self-Healable and Recyclable Polysiloxanes Based on Hierarchical Hard Domains

Room-temperature Self-healable and Reprocessable Polyurethane Elastomers Combined Diels-Alder Bond and Disulfide Bond