Two-Dimensional MoO 2 Nanosheet Composite Hydrogels with High Transmittance and Excellent Photothermal Property for Near-Infrared Responsive Actuators and Microvalves
Zhichao Sun,Cong Wei,Wentao Liu,Hao Liu,Jiahui Liu,Rui Hao,Miaoming Huang,Suqin He
DOI: https://doi.org/10.1021/acsami.1c04110
2021-07-11
Abstract:Stimulus-responsive intelligent hydrogel actuators have highly promising applications in the fields of soft robotics, smart manipulators, and flexible devices. Near-infrared (NIR) light is considered an ideal method to trigger the response behavior remotely and precisely. In order to realize the excellent optical transmittance and photothermal property of NIR-responsive hydrogels at the same time, two-dimensional nonlayered MoO<sub>2</sub> nanosheets (2D-MoO<sub>2</sub>) with excellent photothermal efficiency (62% under an NIR light irradiation of 808 nm), splendid chemistry stability, and low preparation cost are used as photothermal agents and incorporated into the poly(<i>N</i>-isopropylacrylamide) (PNIPAM) hydrogel network, forming the 2D-MoO<sub>2</sub>/Laponite/PNIPAM ternary nanocomposite hydrogel (TN hydrogel). It is remarkable that compared with the GO and MXene hydrogels with the same agent content (1.0 mg mL<sup>–1</sup>) and thickness (1 mm) whose transmittance values are only ∼5% at 600 nm, the TN hydrogel shows a similar NIR-responsive temperature, but much higher optical transmittance (∼53%). Besides, of the three hydrogels with similar transmittance, the TN hydrogel shows a much higher NIR-responsive temperature. The TN hydrogel with a low loading of 2D-MoO<sub>2</sub> (1.5 mg mL<sup>–1</sup>) can produce a significant temperature increase of ∼30 °C after the application of 0.8 W cm<sup>–2</sup> NIR light irradiation for 15 s. Impressively, the TN hydrogel exhibits excellent anti-fatigue property, keeping a fast response and temperature rise behavior even after 50 times of heating–cooling cycles. The flexibly controllable and reversible deformation is realized by a well-designed bilayer structure even in harsh environments. The transparent and asymmetric bilayer hydrogel is further used as a soft manipulator to capture objects visually and accurately. The NIR light-controlled microvalve based on this composite hydrogel is also demonstrated. This work provides a novel kind of transparent hybrid NIR response hydrogel for the further development of smart, programmable, reversible hydrogel-based actuators and soft robotics.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c04110?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c04110</a>.Schematic illustration of the synthesis progress of the MoO<sub>2</sub> nanosheets; TEM images of the MoO<sub>2</sub> nanosheets; Photographs of MXene, GO, and 2D-MoO<sub>2</sub> dispersion before and after heating; The photothermal performance of the 2D-MoO<sub>2</sub> dispersion and the calculation of photothermal conversion efficiency of 2D-MoO<sub>2</sub>; The Super Depth of Field Microscope images of bilayer TN-1.0/NC hydrogel; The SEM images of the NC, TN-0.6, and TN-1.2 hydrogels; The XRD spectra of the NC and TN-1.5 hydrogels. Schematic illustration of the bending angle; Bending behavior of bilayer hydrogel with flower shape in air and water; Bending behavior of the bilayer hydrogel actuator upon NIR irradiation; Schematic illustration of the curvature of the hydrogel actuator (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c04110/suppl_file/am1c04110_si_001.pdf">PDF</a>)The liquid microvalve fabricated by the TN-1.5 hydrogel before and after exposure to NIR irradiation (808 nm, 0.8 W cm<sup>–2</sup>) for 1.5 min (Video S1) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c04110/suppl_file/am1c04110_si_002.mp4">Mp4</a>)The bending behavior of bilayer hydrogel with flower shape (Video S2) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c04110/suppl_file/am1c04110_si_003.mp4">Mp4</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology