Abstract:This study presented the experimental and theoretical results of insulated concrete Sandwich panels with innovative dumbbell-shaped steel fiber-reinforced polymer (FRP) composite bar (SFCB) connectors under flexural load. The influences of FRP thickness and raised thickness of dumbbell ends of connectors, axial compression ratio, the content of vitrified microspheres in the wythes, and loading direction were discussed. The increase in thickness of a glass FRP (GFRP) jacket on the hybrid bar from 2 to 3 mm led to increased initial cracking load, ultimate load, and flexural stiffness of the Sandwich panels by 75, 49, and 16%, respectively. The increase in the thickness of dumbbell ends from 4 to 6 mm led to increased initial cracking load, ultimate load, and flexural stiffness of the Sandwich panels of 18, 46, and 9%, respectively. The incorporation of vitrified microspheres in concrete wythes resulted in a significant increase in the load-carrying capacity of Sandwich panels but decreased ductility. Increased axial compression ratio from 0/1 to 0.2/1 contributed in improving the crack resistance and ultimate loads of Sandwich panels. Further increase of the axial compression ratio to 0.4/1 led to crushing failure of concrete wythe ends. Specimens under negative loads had higher ultimate loads than the counterparts under positive loads. Three-dimensional finite-element (FE) models were developed to simulate Sandwich panel flexural behavior and numerical results compared with the test data. Then, the verified FE model was used to analyze the influence of the arrangement of dumbbell-shaped SFCB connectors. Increased connector spacing from 550 to 650 mm was found to have an insignificant influence on load-deflection responses. Moreover, analytical solutions for deflection of Sandwich panels under combined axial-flexural load were obtained, in which the effect of slipping between the facade and structural wythes and shear deflection were considered. The predicted deflection at the ultimate load agreed well with the test results. This study provided a theoretical basis and design reference for FRP-jacketed steel-composite connectors in applications of Sandwich wall panels with large insulation layer thickness.

Flexural Behaviors and Local Failure Analyses of EPS Foam-Filled GFRC Truss-Core Sandwich Panels

Experimental investigation of mechanical behaviors of EPS foamed concrete-filled pultruded GFRP sandwich panels

Mechanical and thermal insulate behaviors of pultruded GFRP truss-core sandwich panels filled with EPS mortar

Foam-filling Techniques to Enhance Mechanical Behaviors of Woven Lattice Truss Sandwich Panels

Flexural performance of precast geopolymer concrete sandwich panel enabled by FRP connector

Flexural Behavior of Insulated Concrete Sandwich Panels using FRP-Jacketed Steel-Composite Connectors

Flexural Experiment and Design Method of Steel-Wire-Enhanced Insulation Panels

Flexural Behavior of Singly Curved GFRP Sandwich Panel with Polyurethane Foam Core

An Investigation of the Properties of Expanded Polystyrene Concrete with Fibers Based on an Orthogonal Experimental Design

The influence of sizing on the compressive performance of foam-reinforced woven lattice sandwich panels

Structural behavior of load-bearing sandwich wall panels with GFRP skin and a foam-web core

Three-point bending behaviors of the foam-filled CFRP X-core sandwich panel: Experimental investigation and analytical modelling

Experimental and Numerical Analysis of Nonlinear Flexural Behaviour of Lattice-Web Reinforced Foam Core Composite Sandwich Panels

Flexural Performance of Sandwich Beams with Lattice Ribs and a Functionally Multilayered Foam Core

Flexural performance of novel ECC-RC composite sandwich panels

Behavior of sandwich wall panels with GFRP face sheets and a foam-GFRP web core loaded under four-point bending

Mechanical Performance of Foam-Filled Lattice Composite Panels in Four-Point Bending: Experimental Investigation and Analytical Modeling

Experimental and Theoretical Study on Flexural Behaviour of a New UHPC Sandwich Slab

Experimental investigation into the synergetic damage of foam-filled and unfilled corrugated core hybrid sandwich panels under combined blast and fragment loading

Flexural Behavior of Slab-Rib Integrated Bridge Decks with GFRP Skin and Polyurethane Foam Core

Research and Statistical Analysis on Impact Resistance of Steel Fiber Expanded Polystyrene Concrete and Expanded Polystyrene Concrete