Abstract:In this study, a dynamic constitutive model for woven-carbon-fiber-reinforced plastics (CFRP) is formulated by combining dynamic tensile test data and fitting curves and incorporating variation rules established for the modulus of elasticity, strength, and fracture strain with respect to the strain rate. The dynamic constitutive model is then implemented with finite element software. The accuracy and applicability of the dynamic constitutive model are evaluated by comparing the numerically predicted load–displacement curves and strain distributions with the test data. The stress distribution, failure factor, modulus, and strength of the material under dynamic tension are also explored. The results show that the response simulated with the dynamic constitutive model is in good agreement with the experimental results. The strain is uniformly distributed during the elastic phase compared with the DIC strain field. Subsequently, it becomes nonuniform when stress exceeds 600 MPa. Then, the brittle fracture occurs. With the increase in the strain rate, the input modulus decreased, and the tensile strength increased. When the displacement was 0.13 mm, the simulation model was damaged at a low strain rate, and the stress value was 837.8 MPa. When it reached the high strain rate of 800 s−1, no failure occurred, and the maximum stress value was 432.5 MPa. For the same specimen, the strain rate was the smallest on both clamped ends, and the modulus and strength were large at the ends and small in the middle. The fitting curve derived from the test data was completely input into the dynamic constitutive model to better capture the dynamic change in the material properties.

Tension-tension Fatigue Behavior and Its Modelling for Life Estimation of Rivet-Bonding CFRP/CFRP Single Lap Joints

Fatigue failure mechanisms and probabilistic S-N curves for CFRP–steel adhesively bonded joints

Prediction of long-term fatigue life of CFRP composite hydrogen storage vessel based on micromechanics of failure

Residual stress and fatigue behavior of riveted lap joints with various riveting sequences, rivet patterns, and pitches

Experimental and Analytical Study on Residual Stiffness/Strength of CFRP Tendons under Cyclic Loading

Numerical Analysis of High and Low‐cycle Flexural Fatigue for Reinforced Concrete Beams under Full‐range of Varying Amplitudes

Experimental Study and Modeling of Fatigue Life Prediction of Plain Weave Carbon/Polymer Composite under Constant Amplitude Loading

Experimental Research and Analysis on Fatigue Life of Carbon Fiber Reinforced Polymer (CFRP) Tendons

Reliability Fatigue Life and A New S–N Curve Model of Composite Laminates Under Tensile-Tensile Fatigue Load

Experimental Study on Interfacial Bond Behavior between CFRP Sheets and Steel Plates under Fatigue Loading

Modeling the residual strength and fatigue life of carbon fiber composites under constant amplitude loading

Analysis of Residual Stresses Induced by Riveting Process and Fatigue Life Prediction

Fatigue life prediction of fiber reinforced concrete under flexural load

Cyclic elastoplasticity-based life assessment of fatigue crack initiation and subsequent propagation in rib-to-deck welded joints

Fatigue Behaviors and Mechanism-Based Life Evaluation on SPR-bonded Aluminum Joint

Fatigue failure mechanism analysis and life prediction of short fiber reinforced polymer composites under tension-tension loading

Fatigue behaviour analysis of aluminium alloy riveted single-shear lap joints

Stress, damage, and fatigue performance analysis of CFRP/Al double-sided countersunk riveted joints with variable rivet-hole clearance

A Dynamic Constitutive Model and Simulation of Braided CFRP under High-Speed Tensile Loading

Fatigue Behavior of CFRP-Concrete Interface

Fatigue Strength Prediction Of Bolted Joint Structures Of Carbon Fibre Reinforced Polymer Composite Based On The Micromechanics