Ni-Co-Mn complexed 3,4,9,10-perylene tetracarboxylic acid complexes as novel organic electrode material for lithium-ion batteries
Wenfeng Yuan,Mengqian Xu,Lucheng Li,Nei Chen,Jun Chen,Qian Zhang
DOI: https://doi.org/10.1039/d3dt03559j
IF: 4
2023-12-19
Dalton Transactions
Abstract:In order to solve the problems of large solubility, poor conductivity and low active point exposure and utilization rate of organic electrode materials in the electrolyte, in this work, Ni-Co-Mn complexed 3,4,9,10-perylenetetracarboxylic dianhydride (PTCDA-NiCoMn) is prepared by hydrolysis of 3,4,9,10-perylenetetracarboxylic dianhydride (PTCDA) and complexed reactions with Ni, Co and Mn ions. At the same time, graphene is added to in-situ composite with PTCDA-NiCoMn to obtain the graphene in-situ composited Ni-Co-Mn complexed 3,4,9,10-perylenetetracarboxylic dianhydride composites (PTCDA-NiCoMn-G). The prepared PTCDA-NiCoMn exhibits fibrous structure and the number of pore units increases with the expansion of the fibrous structure. After the graphene in situ recombination, shorter PTCDA-NiCoMn tubular fibers are dispersed between the thin layers of graphene, showing a larger surface area, leaving more PTCDA-NiCoMn active components exposed, which would be more conducive to the electrochemical properties. As a result, the initial charge/discharge capacities of PTCDA-NiCoMn and PTCDA-NiCoMn-G electrodes are 1972.9 mAh g-1 and 1806.6 mAh g-1 with initial coulonbic efficiency of 56.3% and 62.52% at 100 mA g-1, respectively. After 200 cycles, the charge/discharge capacities of PTCDA-NiCoMn and PTCDA-NiCoMn-G are 617.0 mAh g-1 and 876.4 mAh g-1 with capacity retention ratio of 51.4% and 73.0% at 100 mA g-1, respectively. Similarly, PTCA-NiCoMn-G electrodes show higher capacities than the PTCA-NiCoMn electrode at different current densities of 0.1 A g-1, 0.2 A g-1, 0.5 A g-1, 1 A g-1, 2 A g-1 and 5 A g-1. The results show that PTCDA-NiCoMn-G electrode displays superior capacity, ICE, cycle and rate behaviors. The complexation of NiCoMn reduces the solubility of the PTCDA active units in the electrolyte, and the in situ recombination of graphene increases the dispersion of the active components, exposes more active sites, and effectively improves the conductive performance, which contributes to the electrochemical properties of PTCDA-NiCoMn-G electrode.
chemistry, inorganic & nuclear