Abstract:Compared with other power storage technologies such as batteries, supercapacitors can attain higher power density, but the situation of lower energy density requires improvement. In this study, in order to maintain the stability of the template structure, zinc ions in the template of ZnO nanosheets were partially dissolved and combined with 2-methylimidazole (2-MI) to form ZnO@ZIF-8 on the residual ZnO by controlling the addition amount of organic ligands. Then the remaining ZnO was continued to be dissolved with 2-MI, and the released zinc ions and the co-added cobalt ions were further integrated with the organic complex to form ZIF-8/67, which can be anchored to two-dimensional monolayer Mxene. Finally, ZIF-8/67 can be etched with nickel nitrate and cobalt nitrate to obtain ZnNiCo LDH@Mxene (ZNC@M) with 2D/2D hierarchical structure. The specific capacitance of ZNC@M can achieve 2011F g −1 (1 A g −1 ). Meanwhile, it has excellent rate performance (10 A g −1 maintained at 68.6 %) and cyclic stability (maintained at 92.8 % after 5000 cycles). Potential window and energy density of the asymmetric supercapacitor (ASC) were obviously improved while composites are applied as cathode and activated carbon (AC) as anode, and KOH solutions with potassium ferricyanide as electrolyte. When the power density of the assembled device is 800–8000 W kg −1 , the energy density is maintained from 65.6 Wh kg −1 to 37.3 Wh kg −1 . In addition, the density of states (DOS), project density of states (PDOS), and energy band changes before and after the addition of Mxene were discussed by using density functional theory (DFT) calculation. The above conclusions confirm that Mxene is beneficial to promote the electron transfer state of ZnNiCo LDH. Therefore, this work demonstrates that the anchoring of micro-sized materials is a powerful approach for the preparation of two-dimensional hierarchical structures.

Self-assembly of Alternating Stacked 2D/2D Ti3C2Tx MXene/ZnMnNi LDH Van Der Waals Heterostructures with Ultrahigh Supercapacitive Performance

MXene-transition Metal Sulfide Composite Electrodes for Supercapacitors: Synthesis and Electrochemical Characterization

High Energy Density of Two-Dimensional MXene/NiCo-LDHs Interstratification Assembly Electrode: Understanding the Role of Interlayer Ions and Hydration

Boosted Electrochemical Performance of Honeycomb-Like NiCu-LDH Nanosheets Anchoring on NiCo<sub>2</sub>S<sub>4</sub> Nanotube Arrays for Flexible Solid-State Hybrid Supercapacitors

Electrostatically self-assembled zeolitic imidazolate framework-67 templated cobalt tungsten layered double hydroxide@MXene nanosheets for superior biocompatible energy storage system

Facile Synthesis of Exfoliated Co-Al LDH-carbon Nanotube Composites with High Performance As Supercapacitor Electrodes.

A heterostructure of NiMn-LDH nanosheets assembled on ZIF-L-derived ZnCoS hollow nanosheets with a built-in electric field enables boosted electrochemical energy storage.

Trimetallic layered double hydroxides with a hierarchical heterostructure for high-performance supercapcitors

Synergistically Coupling of 3D FeNi-LDH Arrays with Ti3C2Tx-MXene Nanosheets Toward Superior Symmetric Supercapacitor

Inlaid layered double hydroxides and MXene composite electrodes with high rate performance as asymmetric supercapacitors

ZnNiCo layered double hydroxide@Mxene with 2D/2D hierarchical structure derived from micro-sized ZIF-8/67 anchored to Mxene for asymmetric supercapacitors

Ti 3 C 2 T x MXene-Coupled NiCo-Layered Double Hydroxide Nanosheets with Entire Contact for High-Performance Supercapacitors

Electrochemical Storage Mechanism of Interstratification-Assembled Ti3C2Tx MXene/NiCo-LDHs Electrode in Alkaline, Acid and Neutral Electrolytes

Facile self-assembly of sandwich-like MXene/graphene oxide/nickel–manganese layered double hydroxide nanocomposite for high performance supercapacitor

High-performance Supercapacitor Materials Based on NiMn-LDH Layered Structures with MXene Layers

Heterostructures of Ni–Co–Al layered double hydroxide assembled on V4C3 MXene for high-energy hybrid supercapacitors

Layered Double Hydroxide with Interlayer Quantum Dots and Laminate Defects for High‐Performance Supercapacitor

Oxygen-Vacancy-Rich NiMnZn-Layered Double Hydroxide Nanosheets Married with Mo 2 CT x MXene for High-Efficiency All-Solid-State Hybrid Supercapacitors

Design and Preparation of NiCoMn Ternary Layered Double Hydroxides with a Hollow Dodecahedral Structure for High-Performance Asymmetric Supercapacitors

Rational Design of Three-Dimensional Interlaced Frameworks with 2D MXene-Ti3C2Tx and 2D ZnCo Bimetallic Hydroxide for Enhanced Sodium-Ion Capacitors

Fe, Co-codoped layered double hydroxide nanosheet arrays derived from zeolitic imidazolate frameworks for high-performance aqueous hybrid supercapacitors and Zn-Ni batteries