Abstract:Magnetic Fe3O4/P (MMA/DVB)((core))-P (St/(GMA/DVB)((shell)) composite microspheres with core-shell structure were prepared by a two-step method. (1) Preparation of the magnetic cores: First, the magnetic miniemulsion composed of organic ferrofluid droplets dispersed in water was obtained by rapid addition of an oil-based magnetite ferrofluid, with a solid content 60 wt%, into the aqueous solution using DNS-86 (polymerizable surfactant) as surfactant in the condition of ultrasonic emulsification. Then, the copolymerization monomers of methyl mathacrylate (MMA) and divinyl benzene (DVB) were injected directly into the magnetic miniemulsion. Because of their hydrophobic character, once the monomers were added into the emulsion, the methyl mathacrylate (MMA) and divinyl benzene (DVB) would have a high tendency to diffuse inside the organic phase of the ferrofluid droplets to form monomer swelling magnetic miniemulsion, Which were supposed to be the main locus for copolymerization. in succession, the temperature was rapidly increased to 70 degrees C and starting the miniemulsion copolymerization to form uniform magnetic latexes. (2) Preparation of the core/shell hybrid polymeric microspheres: Through varying the feeding amount of styrene (St), glycidyl methacrylate (GMA) and DVB, the core-shell structured microspheres were rationally fabricated by the seed emulsion copolymerization using the above magnetic latex as the core emulsion. This preparation process is convenient and effective. Extensive. characterization by X-ray diffraction (XRD), high resolution transmission electron microscopy (HR-TEM), thermogravimetric analysis (TGA) and vibrating sample magnetometer (VSM) showed that the magnetite content of Fe3O4/P(MMA/DVB) composite microspheres was 84 wt %. The magnetite content of the magnetic composite microspheres with core-shell Structure is varied from 20 wt % to 76 wt % by feeding different amount of monomers. The average diameter of the magnetic seeded microspheres and the core-shell composite microspheres is 150 nm and 350 nm, respectively. The functional epoxy groups on the surface of the core-shell composite microspheres can be further modified to load biomolecules.

Preparation Of Superparamagnetic Beta-Cyclodextrin-Functionalized Composite Nanoparticles With Core-Shell Structures

Preparation of superparamagnetic β-cyclodextrin-functionalized composite nanoparticles with core–shell structures

Preparation and Characterization of Cross-Linked Β-Cyclodextrin Polymer/fe 3 O 4 Composite Nanoparticles with Core-Shell Structures

Preparation and Properties of Crosslinked Β-Cd Polymer/Fe3O4 Composite Nanoparctiles with Core-shell Structures

PREPARATION AND CHARACTERIZATION OF MAGNETIC COMPOSITE MICROSPHERES WITH CORE-SHELL STRUCTURE

A facile synthesis of superparamagnetic Fe3O4 supraparticles@MIL-100(Fe) core-shell nanostructures: Preparation, characterization and biocompatibility

Preparation and Characterization of Ω-Functionalized Polystyrene–magnetite Nanocomposites

Preparation of Hybrid Polymer Nanocomposite Microparticles by a Nanoparticle Stabilised Dispersion Polymerisation

Synthesis and characterization of carbon-coated iron core/shell nanostructures

Β-Cyclodextrin-modified Hybrid Magnetic Nanoparticles for Catalysis and Adsorption

A Novel Approach to Preparing Magnetic Protein Microspheres with Core-Shell Structure

Preparation, characterization, and catalytic activity of core/shell Fe3O4@polyaniline@au nanocomposites.

An improved way to prepare superparamagnetic magnetite-silica core-shell nanoparticles for possible biological application

Toward Designer Magnetite/polystyrene Colloidal Composite Microspheres with Controllable Nanostructures and Desirable Surface Functionalities.

PREPARATION AND CHARACTERIZATION OF MONODISPERSE P(St/AA) =COMPOSITE MICROSPHERES WITH HIGH Fe3O4 CONTENT

Synthesis of Cross-Linked Magnetic Composite Microspheres Containing Carboxyl Groups

Preparation and characterization of polymer-coated core–shell structured magnetic microbeads

Preparation of Magnetite Nanoparticles Coated with an Amphiphilic Block Copolymer: A Potential Drug Carrier with a Core-Shell-Corona Structure for Hydrophobic Drug Delivery

Core–shell Structural Iron Oxide Hybrid Nanoparticles: from Controlled Synthesis to Biomedical Applications

Preparation and application of mesoporous Fe/carbon composites as a drug carrier

Synthesis and characterization of multi-functional hybrid magnetite nanoparticles with biodegradability, superparamagnetism, and fluorescence