Abstract:Titanium oxide nanotube arrays (TiO2-NTAs) with different diameters and lengths are prepared by anodization of titanium foils in a water/ethylene glycol solution (5:95 V/V) containing 0.3 wt% NH4F. The effects of the diameters, lengths and crystalline phases of the NTAs on the photocatalytic (PC) activity are systematically evaluated. Larger pore diameter results in higher PC activity. The PC activity increases initially and then decreases with lengths for TiO2-NTAs and the optimal length that yields the highest PC activity is observed to be 6.2 microm. The crystalline phase and corresponding PC activity depend on the calcination temperature and their relationship is also investigated. The amorphous-to-anatase and anatase-to-rutile phase transitions initially occur at 300 and 500 degrees C, respectively. The PC activity of TiO2-NTAs initially increases with calcination temperature from 250 to 500 degrees C and then decreases at higher calcination temperature. The enhanced PC activity observed from the samples annealed at 250-450 degrees C is attributed to the better anatase crystalline structure at higher calcination temperature. The highest PC activity with regard to photodecomposition of methyl orange is observed from TiO2-NTAs calcined at 500 degrees C, which coincides with the anatse-to-rutile phase transformation. The synergistic effect of the anatase TiO2-NTAs and rutile barrier layers facilitate interfacial electron transfer consequently enhancing the PC activity. Further elevation of the calcination temperatures to 550 and 600 degrees C exhibits diminished PC activity because the NTs become shorter due to conversion of the bottom of anatase NTs into rutile film.

Synthesis And Photocatalytic Activity Of Highly Ordered Tio2 And Srtio3/Tio2 Nanotube Arrays On Ti Substrates

Synthesis and Photocatalytic Activity of Highly Ordered TiO2 and SrTiO3/TiO2 Nanotube Arrays on Ti Substrates: Synthesis and Photocatalytic Activity of TiO2 and SrTiO3/TiO2

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Visible-light-driven Photoelectrochemical and Photocatalytic Performances of Cr-doped SrTiO3/TiO2 Heterostructured Nanotube Arrays.

Influence of Structure Parameters and Crystalline Phase on the Photocatalytic Activity of TiO2 Nanotube Arrays.

High-Reactive Heterostructure TiO2/SrTiO3 Nanotube Arrays and Its Photoelectrocatalytic Performance

Preparation and Photoelectrocatalytic Performance of TiO2 Nano-Tubes Arrays Electrode

Tailored TiO2-SrTiO3 heterostructure nanotube arrays for improved photoelectrochemical performance.

Highly ordered anodic TiO 2 nanotube arrays and their stabilities as photo(electro)catalysts

Structural Manipulation of the Photocatalytic Activity of Tio2 Nanotube Arrays

Preparation and Photoelectrocatalytic Performance of TiO<sub>2</sub> Nano-Tubes Arrays Electrode

Preparation Of Tio2 Nanotube Arrays And Their Photoeleetrochemical Properties

Study of Photoelectrochemical Response Behaviors of Highly Ordered TiO2 Nanotube Arrays

Photocatalytic Property under Visible Light of the Nitrogen Doped SrTiO3/TiO2 Nanotube Arrays

Photoelectrochemical Properties of Heterojunction TiO2/SrTiO3 Nanotube Arrays with Exposed TiO2 Highly Reactive Facet

Fabrication of Highly Ordered TiO2 Nanorod/nanotube Adjacent Arrays for Photoelectrochemical Applications.

Facile in Situ Hydrothermal Method for Synthesis of SrTiO3/TiO2Nanostructures with Improved Photoelectrochemical Activities

Heterostructured TiO2 Nanoparticles/Nanotube Arrays: In Situ Formation from Amorphous TiO2 Nanotube Arrays in Water and Enhanced Photocatalytic Activity

Fabrication of Highly Ordered TiO2 Nanotube Arrays and Investigation of Its Photocatalytic Properties

Controllable Synthesis of Well-Ordered TiO2 Nanotubes in a Mixed Organic Electrolyte for High-Efficiency Photocatalysis

Effects of the Structure of TiO[sub 2] Nanotube Array on Ti Substrate on Its Photocatalytic Activity