Abstract:A novel binder jetting process using a mixture of sodium silicate powders and water-based solvent as an inorganic binder system and the corresponding posttreatment process were developed to resolve a contradiction of increased strength with reduced gas volume of sand molds fabricated by traditional binder jetting processes using organic binder. Optimized processing parameters of 50% binder saturation, 10 wt.% sodium silicate powder addition, 0.2 mm layer thickness, 50 vol.% infiltration concentration of alcohol – water solution, 5 min infiltration time, and 250 °C baking temperature buried in glass beads for 1 h were determined by the systematically investigation of printing process. The produced sand mold achieved an excellent performance with a tensile strength of 4.5 MPa and a maximum gas volume of 8.1 L/kg. A casting experiment was carried out to verify the performance of sand mold, the results showed that the casting fabricated using the sand mold prepared by the process studied in this paper has a better surface quality and fewer subcutaneous blowholes in comparison to the traditional process, indicating its excellent industrial application prospects.

Study On Properties And Effects Of A New Heat Cured Inorganic Foundry Binder

Study on Properties of Microwave Hardened Inorganic Phosphate Binder Foundry Sand

Research on New Modified Phosphate Inorganic Resin Binder for Foundry

Research on New Al-Mg-B Compound Phosphate Inorganic Binder for Heat Cured Sand

Research on New Environmental Friendly Heat Cured Sand of Al-Mg-B Compound Phosphate Inorganic Binder

A New Compound Phosphate Heat-Cured Foundry Binder

Research, application and development of inorganic binder for casting process

Superiority of a New Modified Phosphate Casting Binder

A New Phosphate Binder for Making Sand Mold or Core for Aluminum Alloy Castings

Study on Properties of Phosphate Binder No-Bake Sand

Effect of Boron-contaning Modifier on the Properties of Heat-cured Aluminum Phosphate Inorganic Binder-bonded Sand

The Status Quo and Prospect of Environmental Friendly Inorganic Binder for Foundry Use

Effect of Factors on Strength and Stability in No Bake Sand Phosphate Inorganic Binder

Effect of Additives on Heat Hardened Inorganic Solid Foundry Binder

Effect of Magnesium-containing Modifier on the Properties of Boron Aluminum Phosphate Inorganic Binder and Its Heat-cured Molding Sand

Fabrication and posttreatment for inorganic binder jetting sand molds for casting

Study of Environmentally Friendly Phosphate-Bonded No-Bake Sand

Study on Properties of Phosphate Inorganic Resin and No-Bake Mold or Core

Study on Phosphate Foundry Binder Modified by Citric Acid

Laboratory Test Study of Properties of Expansive Soil Improved by Waste Foundry Sand

Study and Application on No Bake Phosphate High Chromite-Corundum Sand