Near Infrared Quantum Cutting Luminescence of Er 3+ /Tm 3+ Ion Pairs in a Telluride Glass

Xiaobo Chen,Song Li,Lili Hu,Kezhi Wang,Guoying Zhao,Lizhu He,Jinying Liu,Chunlei Yu,Jingfu Tao,Wei Lin,Guojian Yang,Gregory J. Salamo

DOI: https://doi.org/10.1038/s41598-017-02244-8

IF: 4.6

2017-01-01

Scientific Reports

Abstract:The multiphoton near-infrared, quantum cutting luminescence in Er 3+ /Tm 3+ co-doped telluride glass was studied. We found that the near-infrared 1800-nm luminescence intensity of (A) Er 3+ (8%)Tm 3+ (0.5%):telluride glass was approximately 4.4 to 19.5 times larger than that of (B) Tm 3+ (0.5%):telluride glass, and approximately 5.0 times larger than that of (C) Er 3+ (0.5%):telluride glass. Additionally, the infrared excitation spectra of the 1800 nm luminescence, as well as the visible excitation spectra of the 522 nm and 652 nm luminescence, of (A) Er 3+ (8%)Tm 3+ (0.5%):telluride glass are very similar to those of Er 3+ ions in (C) Er 3+ (0.5%):telluride glass, with respect to the shapes of their excitation spectral waveforms and peak wavelengths. Moreover, we found that there is a strong spectral overlap and energy transfer between the infrared luminescence of Er 3+ donor ions and the infrared absorption of Tm 3+ acceptor ions. The efficiency of this energy transfer { 4 I 13/2 (Er 3+ ) → 4 I 15/2 (Er 3+ ), 3 H 6 (Tm 3+ ) → 3 F 4 (Tm 3+ )} between the Er 3+ and Tm 3+ ions is approximately 69.8%. Therefore, we can conclude that the observed behaviour is an interesting multiphoton, near-infrared, quantum cutting luminescence phenomenon that occurs in novel Er 3+ -Tm 3+ ion pairs. These findings are significant for the development of next-generation environmentally friendly germanium solar cells, and near-to-mid infrared (1.8–2.0 μm) lasers pumped by GaN light emitting diodes.