Abstract:In this study, 3Cr13 martensitic stainless steel was tempered to three typical strength grades, and the corresponding atmospheric corrosion behavior in a coastal zone of Wanning, China, was investigated. Electrochemical measurements were taken, and the morphology, composition, and structure of the rust formed after natural exposure were analyzed. The results indicated that different microstructures were obtained by tempering at different temperatures, which affected the corrosion behavior. The electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization results show that the 280°C tempered condition was prone to form a better protective passive film compared to the other two higher-temperature tempered conditions. The corrosion rate of 3Cr13 steel tempered at a low temperature of 280°C was markedly lower than that at higher temperatures of 540 and 600°C. The corrosion weight loss of specimens tempered at 540°C and 600°C was over 8 times higher than that of the specimens tempered at 280°C after two years of natural exposure. The thickness of the rust layer formed on the 540- and 600°C-tempered specimens exceeded 40 μm, which was approximately 5 times that of on the 280°C-tempered specimens. The corrosion products formed on tempered 3Cr13 steel were found to vary with the temper conditions. The corrosion products formed on tempered 3Cr13 martensitic stainless steel also varied with the tempering temperature. A rust layer mainly composed of γ-FeOOH and β-FeOOH was formed on 280°C-tempered 3Cr13 steel specimens, while α-FeOOH and Fe3O4 were formed on 540- and 600°C-tempered 3Cr13 steel specimens in addition to γ-FeOOH and β-FeOOH. Distinct pitting corrosion occurred on specimens of all three strength grades specimens during natural exposure. Formation of Cr-rich carbides during high-temperature tempering increased corrosion pit initiation.

Electrochemical Corrosion Behavior And Prediction Of Corrosion Rate For Low Alloy Steel After Tempering Treatment

Electrochemical Corrosion Performance of Low Alloy Steel in Acid Sodium Chloride Solution

Effect of Tempering on Corrosion Behavior and Mechanism of Low Alloy Steel in Wet Atmosphere

Electrochemical Study on Corrosion Process Characteristics of the High-Strength Low-Alloy Steels in NaHSO 3 Solution

Corrosion Behaviors of TWIP Steels in NaCl Solution

Influence of Aging Treatments on Corrosion of ZL114A Alloy

Effect of Tempering Time on Corrosion Resistance of High Co-Ni Steel

Corrosion behavior and electrochemical properties of carbon steel, commercial pure titanium, copper and copper–aluminum–nickel alloy in 3.5% sodium chloride containing sulfide ions

Corrosion Mechanism of Low Alloy Steel in NaCl Solution with CO2 and H2S

Effect of Tempering Treatment on Atmospheric Corrosion Behavior of 3Cr13 Martensitic Stainless Steel in Marine Environment

Effect of aging treatment on electrochemical corriosion behavior of 254SMo stainless steel

Research on Corrosion Behavior of Low Alloy Steel Under the Natural Seawater Wet-Dry Alternate Condition

Effect of Tempered Martensite and Ferrite/Bainite on Corrosion Behavior of Low Alloy Steel Used for Flexible Pipe Exposed to High-Temperature Brine Environment

Corrosion Behavior of Deep Cryogenically Treated AISI 420 and AISI 52100 Steel

CORROSION BEHAVIOR OF RUSTED MILD STEEL UNDER MEANS OF WET/DRY ALTERNATE CONDITIONS

Electrochemical Behavior of Corrosion Resistance Alloys

A Study on Time-Variant Corrosion Model for Immersed Steel Plate Elements Considering the Effect of Mechanical Stress

Effect Of Heat Treatment On Mechanical Property And Electrochemical Corrosion Behavior Of X65 Pipeline Steel In 3.5 Wt.% Nacl

Corrosion Micro- and Macro-Electrochemical Behavior of Rusted Carbon Steel and Weathering Steel

CO2 Corrosion of Low Carbon Steel Under the Joint Effects of Time-Temperature-Salt Concentration

Effect of Tempers on Electrochemical Corrosion Behavior of 7150 Aluminum Alloy Plate in Various Corrosive Media