Effect Of Supercritical Co2 Treatment On The Structure And Properties Of Poly (Ethylene Terephthalate) Fibers

Zc Yu,Hm Lin,Z Zhang

2004-01-01

Abstract:Supercritical CO2 dyeing is one of the most promising dyeing methodsin the 21(st) century. It utilizes CO, at supercritical conditions as dyeing medium, avoiding water pollution and dyes can be collected for recycle. In this paper, melting point, morphology and crystalline structure of PET fibers were investigated through DSC, SEM, WAXS and orientation analysis before and after supercritical CO2 dyeing. Shrinkage has been also studied. The results of the experiments indicate that higher temperature and pressure induce higher melting point and melting enthalpy and higher crystallinity, more oligomer migrate from the inner part of the fiber to the surface. However, orientation of PET fiber decreases slightly after supercritical CO2 treatment. The shrinkage percent increases with increasing temperature and pressure. Pre-heating before dyeing helps to reduce the shrinkage percent of PET fabrics. Moreover, the higher is the heating temperature before dyeing; the lower is the shrinkage percent.