Influence Of Crystal Structure On The Electrochemical Performance Of A-Site-Deficient Sr1-Snb0.1co0.9o3-Delta Perovskite Cathodes

Yinlong Zhu,Ye Lin,Xuan Shen,Jaka Sunarso,Wei Zhou,Shanshan Jiang,Dong Su,Fanglin Chen,Zongping Shao
DOI: https://doi.org/10.1039/c4ra06191h
IF: 4.036
2014-01-01
RSC Advances
Abstract:The creation of A-site cation defects within a perovskite oxide can substantially alter the structure and properties of its stoichiometric analogue. In this work, we demonstrate that by vacating 2 and 5% of A-site cations from SrNb0.1Co0.9O3-delta (SNC1.00) perovskites (Sr1-sNb0.1Co0.9O3-delta, s = 0.02 and 0.05; denoted as SNC0.98 and SNC0.95, respectively), a Jahn-Teller (JT) distortion with varying extents takes place, leading to the formation of a modified crystal lattice within a the perovskite framework. Electrical conductivity, electrochemical performance, chemical compatibility and microstructure of Sr1-sNb0.1Co0.9O3-delta as cathodes for solid oxide fuel cells were evaluated. Among SNC1.00, SNC0.98 and SNC0.95, SNC0.95 (P4/mmm symmetry (#123)) which exhibits a large JT distortion in conjunction with charge-ordering of cobalt (Co) shows the best oxygen reduction reaction (ORR) activity at low temperature while SNC0.98 (P4mm symmetry (#99)), which displays a local JT distortion, shows the poorest performance.
What problem does this paper attempt to address?