Fine Filler Retention Induced By Novel Comb-Like Cationic Pva

Qian Yang,Huining Xiao

2012-01-01

Abstract:Two tailored cationic comb-like poly(vinyl alcohol)s with medium molecular weight, CPVAs, were synthesized via a two-step reaction. PVA was first converted into the macroinitiator for atom transfer radical polymerization (ATRP) by the esterification with alpha-bromoisobutyryl bromide in the solvent 1-methyl-2-pyrrolidione (NMP), followed by the ATRP of [2-(Methacryloyloxy) ethyl] trimethylammonium chloride (MeDMA) along PVA backbone to create comb-like polymer. The arm length of pendant cationic chains was controlled by the molar ratio between the cationic monomer MeDMA and the macroinitiator. The structures of CPAV were confirmed by FT-IR and H-1 NMR. The charge density of CPVAs was measured by colloidal titration using mutek PCD 03. The resulting CPVAs were used as retention aids for fine filler precipitated calcium carbonate (PCC). The retention of the fillers with bleached eucalyptus Kraft pulp was determined using a Mutek DFR-05 drainage freeness retention analyzer equipped with a 150 mesh screen. The results indicated that CPVAs with tailored comb-like structure are promising as effective retention aids for PCC and the rapid flocculation of fine fillers at a relatively dosage. The morphology of PCC flocs, revealed by SEM visualization, further confirmed that the improved retention of PCC was mainly attributed to chemical flocculation between fibers and PCC particles induced by CPVAs.