Abstract:Ferric ions present in an acidic aqueous suspension of TiO2 can promote significantly the photocatalytic degradation of a textile dye X3B upon UV light irradiation (λ ≥ 320 nm). The initial rate of X3B degradation was observed to increase exponentially with the initial concentration of Fe(III). However, this enhancement disappeared as all ferric species were transferred into ferrous ions, and after that the degradation of X3B proceeded via a regular pathway of photocatalysis. Several control experiments revealed that the beneficial effect of Fe(III) was attributed mainly to electron trapping at the semiconductor surface, whereas the contribution from homogeneous Fe(III) photolysis, capable of producing hydroxyl radicals, was not significant. In the liquid phase, more than 98.2% of Fe(II) was detected, implying that the involvement of (Photo)-Fenton reaction was less possible. On the other hand, the ferrous ion, once produced, exhibited no obvious effect on X3B degradation, but its formation became faster in the presence of X3B, suggesting that hole oxidation of X3B might be involved as well. Both Fe(III) and X3B were adsorbed strongly on the catalyst surface, allowing efficient separation and utilization of the electron-hole pairs, whereas Fe(II) was hardly adsorbed, which probably was one of the reasons that Fe(II) could not be re-oxidized in situ by hole or other reactive species generated in the system. Moreover, the increase in the initial pH from 1.6 to 3.7 did not affect obviously the initiate rate of X3B degradation, but led to significant decrease in the initial rate of Fe(II) formation. Together with the exponential increase of Fe(II) formation rate with initial Fe(III) concentration, the primary evidence suggests that the efficiency of electron trapping by Fe(III), similar to Fe(III) photolysis, is also dependent of ferric species polymerization on the surface. The results obtained in this work will be relevant to the study on Fe-doped photocatalyst.

Study On The Enhanced Mechanism Of Tio2 Photocatalysis By Fe3+

Mechanism of Enhanced Photocatalysis of TiO2 by Fe3+ in Suspensions

Enhanced photocatalytic degradation of sulfadiazine by Fe3 + in aqueous TiO2 suspension

Influence of Fe2o3 Doping on Morphology and Photocatalytic Activity of Tio2 Prepared by Adsorption Phase Synthesis

Oxidation of Sulfonamides in Aqueous Solution by UV-TiO2-Fe(VI)

Titanium Dioxide-Supported Iron Species with Efficiently Photocatalytic Performance

A New Role For Fe(3+) In Tio(2) Hydrosol: Accelerated Photodegradation Of Dyes Under Visible Light

Structure Influence of Fe~(3+)-TiO_(2)/SiO_(2) Film on the Photocatalytic Properties

Structure influence of Fe3+ doped TiO2/SiO2 film on the photocatalytic properties

Fe 3+-assisted photocatalytic oxidation of sulfamethazine in tio 2 suspended solution

Photonic, and Photocatalytic Behavior of Tio2 Mediated by Fe, Co, Ni, N Doping and Co-Doping

Study on the mechanisms of photoinduced carriers separation and recombination for Fe3+–TiO2 photocatalysts

Enhanced photocatalytic activity of Fe-, S- and N-codoped TiO2 for sulfadiazine degradation

Synthesis, Characterization, and Photocatalysis of Fe-Doped : A Combined Experimental and Theoretical Study

Reaction mechanism of Fe(III) participated photocatalytic degradation of X3B over TiO2

A New Role for Fe<sup>3+</sup>in TiO<sub>2</sub>Hydrosol: Accelerated Photodegradation of Dyes under Visible Light

Effect of Fe doping on crystalline phase, structure and photocatalytic properties of TiO2 thin films

Synthesis and Characterization of Fe-N-S-Tri-Doped Tio2 Photocatalyst and Its Enhanced Visible Light Photocatalytic Activity

Effect of Surface Fe2O3 Clusters on the Photocatalytic Activity of TiO2 for Phenol Degradation in Water.

Exploring the impact of Fe3+ ions on TiO2 nanostructures to enhance photocatalytic efficiency

Enhanced Photocatalytic Activity and Stability of Nano-Scaled TiO2 Co-Doped with N and Fe