Comparative study of poly tannic acid functionalized magnetic particles before and after modification for immobilized penicillin G acylase
Hongyi Tu,Kaikai Gao,Boyuan Zhang,Zhenbin Chen,Pingbo Wang,Zhizhong Li
DOI: https://doi.org/10.1080/09205063.2021.2021352
2021-12-30
Abstract:In this work, Fe<sub>3</sub>O<sub>4</sub> nanoparticles (NPs) was synthesized by inverting microemulsion method. After that, based on the physical and chemical properties of tannic acid (TA), poly tannic acid (PTA) was coated on Fe<sub>3</sub>O<sub>4</sub> NPs surface. Fe<sub>3</sub>O<sub>4</sub> NPs coated with PTA, on the one hand, was used to immobilize Penicillin G acylase (PGA) by physical adsorption. On the other hand, it was modified by glutaraldehyde (GA). GA grafting rate (<i>G<sub>r-GA</sub></i>) was optimized, and the <i>G<sub>r-GA</sub></i> was 30.0% under the optimum conditions. Then, through the Schiff base reaction between the glutaraldehyde group and PGA amino group, this covalent immobilization of PGA was further realized under mild conditions. Finally, the structures of every stage of magnetic composites were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), vibration magnetometer (VSM) and transmission electron microscopy (TEM), respectively. The results indicated that the enzyme activity (<i>EA</i>), enzyme activity recovery (<i>EAR</i>) and maximum load (<i>ELC</i>) of the immobilized PGA were 26843 U/g, 80.2% and 125 mg/g, respectively. Compared to the physical immobilization of PGA by only coating PTA nanoparticles, further modified nanoparticles by GA showed higher catalytic stability, reusability and storage stability.
engineering, biomedical,materials science, biomaterials,polymer science