Abstract:Compressive deformation behaviors of alpha-Si(3)N(4)w/4032Al metal-matrix composite and the corresponding 4032 Al alloy have been measured at strain rates of 0.37s(-1) in semi-solid state. Based on the Al-Si phase diagram, the basic microstructure is primary aluminum solution and Al-Si eutectic phase for 4032 Al alloy. The morphology of the eutectic Al-Si alloy was found to play an important role in the hot compressive deformation of the materials. The results indicate that the discrepancy of the flow stress between the Si(3)N(4)w/4032 Al composite and 4032 Al alloy decreases with increasing temperature. When the 4032 Al alloy is compressed at 560 degreesC, partial melting was found to start at the grain boundaries, followed by an apparent decrease in the proportion of eutectic Al-Si phase. When the 4032 Al alloy is compressed at 580 degreesC, the liquid with Al-Si eutectic phase brakes away towards the surface of the specimen. Quantitative microscopy was used to determine the statistical characteristics of the average secondary dendrite arm spacing (DAS) and the Al-Si eutectic phase.

Compressive Deformation Of A -Si3n4 W/4032ai Composite At Temperatures Around The Solidus Of The Matrix Alloy