Effects of Pack Cementation Aluminizing and Vapor Aluminizing on Oxidation Behavior of P92 Steel in Saturated Steam at 650 C

Zhou Yongli,Lu Jintao,Huang Jinyang,Yang Zhen,Yuan Yong,Gu Yuefeng,Zhao Qinxin

DOI: https://doi.org/10.11933/j.issn.1007-9289.20190620001

2020-01-01

China surface engineering

Abstract:Surface aluminizing technology is a cost-effective method which can improve the high-temperature steam oxidation resistance of substrate alloys without worsening their mechanical performance. Aluminide coatings were obtained on P92 steel surface by low- temperature pack cementation and vapor aluminizing process. The oxidation behavior of the aluminide coatings in saturated steam at 650 degrees C was investigated by oxidation weight increase method, SEM together with XRD analysis. Results show that the P92 steel has a poor oxidation resistance. A double-layered oxide scales consisting of nodular-typed Fe-rich outer layer and FeCr2O4 inner layer formed on P92, and the outer Fe-rich oxide film begin to peel off after 300 h. As for low-temperature pack cementation aluminizing, a thin beta-FeAl layer grows on P92 steel, and an extremely thin (<0. 2 mu m) protective alpha-Al2O3 scale forms on beta-FeAl layer. A single Fe3Al layer forms after vapor aluminizing. A mixed oxides conpose of an outer Fe3O4+Fe2O3 of about 1. 3 mu m and an inner Al2O3 scale after 500 h oxidation. Aluminide coatings prepared on P92 steel through both low-temperature pack cementation and vapor aluminizing process can improve the steam oxidation resistance of P92 steel significantly.