Abstract:The greatest difficult step in the cleavage process presents in term of 'critical event'. In this paper results of series investigations on the critical event for cleavage of HSLA steel are presented. It reveals that basically the critical event for cleavage of notched specimens of HSLA steels at low temperature (lower than -130oC) is the 'propagation of a ferrite grain-sized crack'. The criterion for crack propagation can be presented by following formula σyy =Q σflow = Q(σy+ ∆ σy) σ ≥ f. Any variation, which makes above formula to be satisfied easier, may induce the change of critical event from propagation of a grain-sized crack to propagation of a second phase particle-sized crack and further to the crack nucleation. A precrack is more acute than a notch, thus it increases the stress intensification factor Q and σyy, which can propagate a second phase particle-sized crack even though it is much shorter than a grain-sized crack. Decreasing the test temperature and increasing the loading rate, both increase σy and make the term in the left side of above formula easier to reach the σf. The prestrain produces a increment of ∆ σy by work hardening, which put the same effect as increasing σy. Increasing grain sizes acts from other hand to decrease σf, which also makes the formula to be satisfied easier. In essence, critical event can be transformed to the 'propagation of a second phase particle-sized crack' and further to the 'crack nucleation' by increasing the acuity of defects (in precracked specimen), coarsening the grain size, decreasing the test temperature, raising the loading rate, and subjecting specimens to pre-strain.

Advances In The Mechanism Of Cleavage Fracture Of Low Alloy Steel At Low Temperature .1. Critical Event

Advances in the mechanism of cleavage fracture of low alloy steel at low temperature. Part I: Critical event

Advances in the mechanism of cleavage fracture of low alloy steel at low temperature. Part II: Fracture model

Study of mechanism of cleavage fracture at low temperature

Further Study on the Mechanism of Cleavage Fracture at Low Temperatures

Change of critical events of cleavage fracture with variation of microscopic features of low-alloy steels

Further investigation of critical events in cleavage fracture of C-Mn base and weld steel

CHANGE OF CRITICAL EVENT FOR CLEAVAGE FRACTURE OF HSLA STEEL

Cleavage Fracture Criterion Of Low Alloy Steel And Weld Metal In Notched Specimens

Cleavag Fracture Criterion of Low Alloy Steal and Weld Metal in Notched Specimens

Advances in the mechanism of cleavage fracture of low alloy steel at low temperature. Part III: Local fracture stress σ

Mechanism of detrimental effects of carbon content on cleavage fracture toughness of low-alloy steel

A Theory of Cleavage Characteristic Stress on Low-Temperature Cleavage Fracture in Mild Steel-a Review

3007 - CLEAVAGE INITIATION MECHANISM IN NOTCHED SPECIMENS OF STEEL WITH CARBIDES AND INCLUSIONS

Meso-scopic Mechanical Analysis of Effect of Initial Damage on Cleavage Fracture Toughness of Steel at Low Temperature

A Comparison of Fracture Behavior of Low Alloy Steel with Different Sizes of Carbide Particles

Micromechanism of the transition of fibrous cracking to cleavage of C-Mn base and weld steel

On locations initiating cleavage fracture in precracked specimens of low alloy steel and weld metal

Investigation of cleavage fracture initiation in notched specimens of a C–Mn steel with carbides and inclusions

Crack propagation behavior of dual-phase steel at low temperature

MECHANISM OF CLEAVAGE FRACTURE OF HSLA STEEL