Abstract:Photocatalytic oxidation technology is an emerging technology for gas-phase pollution control, which using semiconductor TiO2 as photocatalyst. Nitrogen dioxide and sulfur dioxide are the major city air contaminant and presents a significant health effect. The environmental pollutions of those contaminants have not been improved in recent 20 years and had become a major social problems. Nitrogen dioxide and sulfur dioxide can be photocatalytic degraded into SO42- and NO3- respectively using TiO2 as photocatalyst.Due to the conventional powder catalysts suffer from disadvantages in stirring during the reaction and separation after the reaction. Preparation of the catalysts coated as thin films make it possible to overcome these disadvantages and extend it to industrial application. In this paper, the German Degussa P-25 TiO2 was used as photocatalyst. The thin films were prepared on the 8 pieces of 1 X 0.5 square meter common glasses via physical method. The effect of initial concentration of reactants on photocatalytic purifying efficiency was studied. The experiment of photocatalytic oxidation was fulfilled in a 2x2x1 cubic meter airproof container made of stainless steel. The commercial ultraviolet lamps were used as light source. The concentration of volatile contaminants varied from 0.5similar to5PPM. The changes of contaminant concentration were measured every two minutes by SO2 analyser and NOx analyzer separately, which was produced by American thermal electron company.The experimental results show that photocatalytic degradation rate increased with increasing initial concentration of NO2 and SO2. The L-H kinetic model was successfully applied to correlate the obtained data.

The Photocatalytic Degradation Of Indoor Air Contamiants Using Thin Film Tio2 Photocatalyst