Abstract:A new anticoagulant agent was prepared by introducing sulfate groups into corn stover xylan through homogeneous reactions. Three organic solvents, N, N-dimethylformamide (DMF), dimethyl sulfoxide (DMSO) and formamide (FA), were adopted as reaction media, with the assistance of LiCl. Structural characterization by FT-IR and (CNMR)-C-13 showed that xylan sulfate (XS) could be successfully synthesized with SO3.Pyridine (SO3.Py) complexes sulfation reagent in the three media. The effect of sulfation temperature, sulfation time, media type and molar ratio of -SO3/-OH on the degree of substitution (DS) and degree of the polymerization (DP) were studied. DMF/LiCl were more effective than DMSO/LiCl and FA/LiCl in preparation of xylan sulfate with high DS. The optimal conditions for sulfation were obtained when SO3.Py complex was added to DMF/LiCl with -SO3/-OH ratio of 1.5:1 and maintained at 50 degrees C for 3h. Degree of polymerization of xylan was decreased during the sulfation process and DMF/LiCl offered the least xylan degradation as compared with DMSO/LiCl or FA/LiCl. Anticoagulant activities of the resultant xylan sulfates with different DS were evaluated by using activated partial thromboplastin time (APTT), thrombin time (TT), and prothrombin time (PT). Results indicated that the introducing of sulfate groups into xylan did endow the polysaccharides with anticoagulant activity. The APTT and TT of XS with DS of 1.20 reached 141 and 45.3s at a dosage of 20g/mL, while the APTT and TT values for the blank sample were only 35.5 and 15.6s. Furthermore, coagulation time was prolonged with the increase of DS and the concentration of XS. Our findings provide new insights into the value-added utilization of agricultural biomass.

Synthesis And Characterization Of Sulfonic Groups Bagasse Xylan Salicylate

Synthesis and Characterization of Bagasse Xylan Chlorosulfonate from the Chlorosulfonic Acid/Pyridine Method

Synthesis and Characterization of Crosslinking Etherification Bagasse Xylan

Preparation and characterization of double activity sulfate-gallate bagasse xylan

Synthesis and nondestructive detailed structure characterization of carboxymethyl xylan from bagasse

Influencing Factors And Conditions On The Synthesis Of Double Activity Sulfate-Gallate Bagasse Xylan

Synthesis and Characterization of Hydrophobically Modified Xylans

Synthesis and characterization of composite functional derivative of ascorbic acid mono ester/acrylic acid/acrylamide grafted onto bagasse xylan gallate

Synthesis And Characterization Of Hemicellulosic Derivatives With Novel Bifunctional Groups In Butanol Medium

Synthesis and Characterization of Periodate-Oxidized Polysaccharides: Dialdehyde Xylan (DAX).

A Novel Process for Preparation of (1→3)-Β-d-glucan Sulphate by a Heterogeneous Reaction and Its Structural Elucidation

Synthesis of Acid-Functionalized Composite Via Surface Deposition of Acid-Containing Amorphous Carbon

Preparation, Characterization and in Vitro Anticoagulant Activity of Corn Stover Xylan Sulfates.

SULFATION OF BIRCH WOOD XYLAN WITH SULFAMIC ACID IN THE PRESENCE OF ACTIVATORS: EXPERIMENT AND THEORY

Preparation and characterization of hemicellulosic derivatives containing carbamoylethyl and carboxyethyl groups.

Per-O-acylation of Xylan at Room Temperature in Dimethylsulfoxide/n-Methylimidazole

Carboxymethyl Xylan - Control of Properties by Synthesis

Glycidyl methacrylate derivatized xylan-rich hemicelluloses: synthesis and characterizations

Mechanocatalytic Solvent-Free Esterification of Sugarcane Bagasse

Synthesis and structure characterization of octenyl succinic acid cellulose ester

A New Method for Enzymatic Synthesis of Xylose Diester in Two-solvent Medium and its Structural Identification