Features of Structure, Magnetic State and Electrodynamic Performance of SrFe 12−x in X O 19

V. A. Turchenko,S. V. Trukhanov,V. G. Kostishin,F. Damay,F. Porcher,D. S. Klygach,M. G. Vakhitov,D. Lyakhov,D. Michels,B. Bozzo,I. Fina,M. A. Almessiere,Y. Slimani,A. Baykal,D. Zhou,A. V. Trukhanov

DOI: https://doi.org/10.1038/s41598-021-97684-8

IF: 4.6

2021-01-01

Scientific Reports

Abstract:Indium-substituted strontium hexaferrites were prepared by the conventional solid-phase reaction method. Neutron diffraction patterns were obtained at room temperature and analyzed using the Rietveld methods. A linear dependence of the unit cell parameters is found. In 3+ cations are located mainly in octahedral positions of 4f VI and 12 k. The average crystallite size varies within 0.84–0.65 μm. With increasing substitution, the T C Curie temperature decreases monotonically down to ~ 520 K. ZFC and FC measurements showed a frustrated state. Upon substitution, the average and maximum sizes of ferrimagnetic clusters change in the opposite direction. The M r remanent magnetization decreases down to ~ 20.2 emu/g at room temperature. The M s spontaneous magnetization and the k eff effective magnetocrystalline anisotropy constant are determined. With increasing substitution, the maximum of the ε / real part of permittivity decreases in magnitude from ~ 3.3 to ~ 1.9 and shifts towards low frequencies from ~ 45.5 GHz to ~ 37.4 GHz. The maximum of the tg(α) dielectric loss tangent decreases from ~ 1.0 to ~ 0.7 and shifts towards low frequencies from ~ 40.6 GHz to ~ 37.3 GHz. The low-frequency maximum of the μ / real part of permeability decreases from ~ 1.8 to ~ 0.9 and slightly shifts towards high frequencies up to ~ 34.7 GHz. The maximum of the tg(δ) magnetic loss tangent decreases from ~ 0.7 to ~ 0.5 and shifts slightly towards low frequencies from ~ 40.5 GHz to ~ 37.7 GHz. The discussion of microwave properties is based on the saturation magnetization, natural ferromagnetic resonance and dielectric polarization types.