Effects Of Salts On Hydrophilicity Of Edible Soy Protein Isolate Films
Wang Weina,Xiong Jian,Ye Jun
2010-01-01
Abstract:As functional films, soy protein isolate (SPI) films have been accorded more and more attention, because SPI is low cost and SPI films have good elasticity, biodegradability, transparency, and high barrier properties against oxygen and oil at low relative humidity. However, there is some limitation in the SPI films. The biggest problem lies in its relatively high moisture sensitivity. To modify the moisture resistance, we studied the effects of NaCl, Na2CO3, Na2S2O3, Na3PO4, Na4P2O7, ZnCl2 and FeCl3 on SPI films, which involves the water content (WC), total soluble matter (TSM), water vapor permeability (WVP) and dynamic contact angle (DCA). The results showed that, compared with the SPI film, the WC of SPI films with NaCl and FeCl3 increased 7.4 % and 15.5 %, however that with Na4P2O7, Na2S2O3, Na3PO4, Na2CO3 and ZnCl2 decreased WC by 18.8 %, 18.9 %, 3.8 %, 7.6% and 16.1 % respectively. The TSM of SPI films with NaCl and Na2S2O3 increased slightly, but Na3PO4, Na2CO3, Na4P2O7, ZnCl2 and FeCl3 made TSM diminish 32.3 %, 13.7 %, 7.1 %, 12.7 % and 23.9 % respectively. The WVP of SPI films with Na3PO4, Na4P2O7, Na2CO3, Na2S2O3 and ZnCl2 rose 88.9 %, 51.4 %, 36.5 %, 28.7 % and 21.0 % respectively, but NaCl had no influence on the WVP. Moreover, FeCl3 made the WVP of SPI film decrease slightly and the DCA of the SPI films with NaCl, Na2CO3, Na2S2O3 and FeCl3 in both polar and nonpolar solvent decreased, respectively, but the DCA of that with Na3PO4, Na4P2O7 and ZnCl2 was just the opposite. The results indicated that the hydrophilicity of SPI edible films could be modified and improved by blending with some salts.