Development and electrochemical investigations of enhanced corrosion-resistant Polyvinylcarbazole-TiO 2 hybrid nanocomposite coatings on 316 L SS for marine applications

N. Elangovan,A. Srinivasan,S. Pugalmani,M. Kalaiyarasan,N. Rajendran,A.H. Seikh,N. Rajendiran

DOI: https://doi.org/10.1016/j.surfcoat.2024.130628

IF: 4.865

2024-03-12

Surface and Coatings Technology

Abstract:The present study focuses on evaluating the corrosion resistance of 316 L stainless steel substrates with Polyvinylcarbazole (PVK)/TiO 2 hybrid nanocomposite coatings (HNC). Using the chronoamperometry approach, the HNC were electrochemically synthesized on 316 L stainless steel substrates, incorporating various weight (%) 1 %, 2 %, 3 % of TiO 2 nanoparticles into the PVK matrix. The findings of the surface morphology investigation verified that the 316 L SS had a dense and smooth PVK/TiO 2 coating. A low surface roughness and high contact value of the PVK/TiO 2 coatings are also responsible for the decrease in corrosion rate of the 316 L SS. The corrosion protection efficiency of the PVK/TiO 2 HNC were investigated through open circuit potential (OCP) measurement, potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) analysis in 3.5 wt% NaCl solution. The corrosion rate obtained from the polarization studies of the HNC coatings as follows PVKT-2 < PVKT-3 < PVKT-1 < PVK < 316 L SS. Results revealed that an optimal loading of 2 wt% TiO 2 nanoparticles significantly enhanced the corrosion resistance of the coating. The enhanced electrochemical impedance response for PVK/TiO 2 coatings was verified by EIS experiments. The study demonstrates that the incorporation of TiO 2 nanoparticles into the PVK matrix effectively creates a barrier layer at the coating-metal interface, inhibiting the entry of aggressive ions. Microhardness studies revealed the increase in hardness value of the PVK and PVK/TiO 2 coatings indicated the protective nature of the coating and provided high mechanical strength to 316 L SS. The tape adhesion tests carried out on the coated specimens also indicated a good adhesion of the PVK/TiO 2 on the 316 L SS surface.

physics, applied,materials science, coatings & films