Phase Modulation of (1T‐2H)‐MoSe2/TiC‐C Shell/Core Arrays via Nitrogen Doping for Highly Efficient Hydrogen Evolution Reaction
Shengjue Deng,Fan Yang,Qinghua Zhang,Yu Zhong,Yinxiang Zeng,Shiwei Lin,Xiuli Wang,Xihong Lu,Cai‐Zhuang Wang,Lin Gu,Xinhui Xia,Jiangping Tu
DOI: https://doi.org/10.1002/adma.201802223
IF: 29.4
2018-07-05
Advanced Materials
Abstract:Tailoring molybdenum selenide electrocatalysts with tunable phase and morphology is of great importance for advancement of hydrogen evolution reaction (HER). In this work, phase- and morphology-modulated N-doped MoSe<sub>2</sub> /TiC-C shell/core arrays through a facile hydrothermal and postannealing treatment strategy are reported. Highly conductive TiC-C nanorod arrays serve as the backbone for MoSe<sub>2</sub> nanosheets to form high-quality MoSe<sub>2</sub> /TiC-C shell/core arrays. Impressively, continuous phase modulation of MoSe<sub>2</sub> is realized on the MoSe<sub>2</sub> /TiC-C arrays. Except for the pure 1T-MoSe<sub>2</sub> and 2H-MoSe<sub>2</sub> , mixed (1T-2H)-MoSe<sub>2</sub> nanosheets are achieved in the N-MoSe<sub>2</sub> by N doping and demonstrated by spherical aberration electron microscope. Plausible mechanism of phase transformation and different doping sites of N atom are proposed via theoretical calculation. The much smaller energy barrier, longer HSe bond length, and diminished bandgap endow N-MoSe<sub>2</sub> /TiC-C arrays with substantially superior HER performance compared to 1T and 2H phase counterparts. Impressively, the designed N-MoSe<sub>2</sub> /TiC-C arrays exhibit a low overpotential of 137 mV at a large current density of 100 mA cm<sup>-2</sup> , and a small Tafel slope of 32 mV dec<sup>-1</sup> . Our results pave the way to unravel the enhancement mechanism of HER on 2D transition metal dichalcogenides by N doping.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology