Flow Stress, Microstructural Evolution, and Constitutive Analysis During High-Temperature Deformation in Mg-4.4Li-2.5Zn-0.46Al-0.74Y Alloy

Cao Furong,Ding Xin,Xiang Chao,Shang Huihui

DOI: https://doi.org/10.11900/0412.1961.2020.00306

IF: 1.797

2020-01-01

ACTA METALLURGICA SINICA

Abstract:Mg-Li alloys have potential applications in the aerospace, military, electronics, and automobile fields due to their superlight density, extremely high specific stiffness, high specific strength, damping, and electromagnetic shielding properties. Due to the limited slip systems of Mg and hcp-structured alpha(Mg) at room temperature, magnesium and alpha(Mg)-based alloys are difficult to deform; thus, it is significant to investigate the high temperature deformation behavior to address this issue. Thus, in this study, an ultralight alpha(Mg)-based Mg-4.4Li-2.5Zn-0.46Al-0.74Y alloy was fabricated via multi-directional forging and rolling, and its flow stress, microstructural evolution, constitutive modeling, and deformation mechanism at elevated temperatures were investigated by tensile tests, OM, and XRD. The results indicate that the grain refinement mechanism of this alloy processed by multi-directional forging (MDF) exhibits mechanical shearing fragmentation and dynamic recrystallization (DRX). Additionally, the flow stress results demonstrate that strain-hardening occurred at 623 K due to grain coarsening, and microstructural evolution reveals that dynamic recovery and DRX occurred at tensile temperatures of 523-573 K; however, grain coarsening primarily appeared at 573 K (or more). XRD analysis demonstrates that this alloy comprised alpha(Mg), beta(Li), Al2Y, Al12Mg17, LiAl, and Mg2Y phases, and hyperbolic sine constitutive analysis reveals that the stress exponent was 4.4 and the activation energy for deformation was 120.40 kJ/mol. The calculated results for dislocation density, number of dislocations in a grain, and atomic diffusion at 623 K and 1.67 x 10(-4) s(-1) corresponding to elongation-to-failure of 240% indicate that dislocation creep controlled by lattice diffusion governed the deformation mechanism under this condition. Predictions by grain growth models indicate that the calculated grain sizes were in good agreement with the practical grain sizes at 623 K and 1.67 x 10(-4) s(-1) when the grain growth factor was equal to 2 and proportional factor was 0.2.