Phosphorus-doped Molybdenum Carbide/mxene Hybrid Architectures for Upgraded Hydrogen Evolution Reaction Performance over a Wide Ph Range

Yi Tang,Chenhui Yang,Minhao Sheng,Xingtian Yin,Wenxiu Que,Joel Henzie,Yusuke Yamauchi

DOI: https://doi.org/10.1016/j.cej.2021.130183

IF: 15.1

2021-01-01

Chemical Engineering Journal

Abstract:Annealing atmosphere strongly affects the structure of phosphorus-doped molybdenum carbide (P-Mo2C) nanodots hybridized with Ti3C2 MXene flakes and modulates its performance in the hydrogen evolution reaction. It is discovered that the nanohybrids undergo partial oxidation when they are annealed in N-2, while retaining similar nanostructures when they are annealed in H-2/Ar, Ar, and NH3. More importantly, compared with the nanohybrids annealed in Ar, NH3, and N-2, the nanohybrid annealed in H-2/Ar delivers the best HER performances, which delivers overpotentials (eta(10)) of 172 and 219 mV at 10 mA cm(-2), and Tafel slopes of 56.2 and 63.3 mV dec(-1) in 0.5 M H2SO4 and 1.0 M KOH, respectively. The excellent HER performance could be attributed to optimal P-Mo2C nanodots for more accessible reactive sites, highly conductive Ti3C2 matrix for accelerated electron transfer, as well as N-doped carbon for more active centers. This work may shed light on developing the promising MXenes-based electrocatalysts by manipulating annealing atmosphere.