Migration, Transformation and Solidification/stabilization Mechanisms of Heavy Metals in Glass-Ceramics Made from MSWI Fly Ash and Pickling Sludge

Shizhen Zhao,Quan Wen,Xiaoyan Zhang,Bo Liu,Shengen Zhang
DOI: https://doi.org/10.1016/j.ceramint.2021.04.172
IF: 5.532
2021-01-01
Ceramics International
Abstract:In consideration of recycling solid waste to achieve high value-added products, glass-ceramics have been fabricated from municipal solid waste incineration (MSWI) fly ash, pickling sludge (PS), and waste glass (WG) by melting at 1450 degrees C firstly to achieve parent glass and then crystallizing at 850 degrees C. Results demonstrated that heavy metals have been well solidified in the prepared glass-ceramics, and relatively/extremely low leaching concentrations of heavy metals have been detected. The synthetic toxicity index of heavy metals has been greatly reduced from 7-18 to <3.2 after crystallization treatment, and the leaching concentrations of Cr, Ni, Zn, Cu, and Pb are 0.15, 0.05, 0.26, 0.12, 0.19 mg L-1 respectively. Chemical morphology analysis, principal component analysis, TEM and EPMA were utilized to clarify the migration, transformation, and solidification mechanism of heavy metals from the as-received solid wastes. The major heavy metals, Cr and Ni which is responsible for the most toxicity, mainly exist in form of the oxidation state and residual state in parent glass, while the residual state in the glass-ceramics. The solidification performance was mostly positively correlated with the form of residue state, which the stability of heavy metals in glass-ceramics is improved. The solidification mechanism of heavy metals in glass-ceramics could be explained by the combination of chemical solidification/stabilization and physical coating. The TEM and EPMA confirmed that Cr and Ni mainly exist in the spinel crystalline (NiCr2O4, Fe0.99Ni0.01Fe1.97Cr0.03O4) by solid solution or chemical substitution, and a small amount of Cr in the diopside phase. Pb, Cu, and Zn are homogenously dispersed in the glass-ceramics, which is considered as physical coating solidification.
What problem does this paper attempt to address?