Synergistic Lithium Storage in Silica–Tin Composites Enables a Cycle-Stable and High-Capacity Anode for Lithium-Ion Batteries
Xuli Ding,Daowei Liang,Xin Ai,Hongda Zhao,Ning Zhang,Xiaojing Chen,Jiahao Xu,Hui Yang
DOI: https://doi.org/10.1021/acsaem.1c00023
IF: 6.4
2021-02-15
ACS Applied Energy Materials
Abstract:Silica (SiO<sub>2</sub>) is considered as a promising candidate anode material for next-generation lithium-ion batteries (LIBs) owing to its low cost, abundant reserve on Earth, and relatively high theoretical specific capacity. However, the development of SiO<sub>2</sub>-based anode materials has been impeded by their poor electrical conductivity and sluggish charge-transfer kinetics. Herein, porous SiO<sub>2</sub>/tin (SiO<sub>2</sub>@Sn) composites with tunable SiO<sub>2</sub> to Sn molar ratios are fabricated using a scalable, simple, and low-cost ball-milling and low-temperature thermal-melting combined method. It is found that the Sn phase can significantly improve the diffusion and migration kinetics of Li in the composites, whereas the SiO<sub>2</sub> to Sn molar ratio plays a key role in the mechanical integrity and subsequent cycling behaviors of the composite electrodes. By optimizing the molar ratio of SiO<sub>2</sub>/Sn to 10:1, the synergistic effect of Li storage between SiO<sub>2</sub> and Sn can lead to the simultaneous achievement of improved Li kinetics and ensured mechanical integrity, contributing to the excellent electrochemical performance of the composite with a large reversible capacity of 613 mAh g<sup>–1</sup> at 100 mA g<sup>–1</sup>, a remarkable rate capability of 450 mAh g<sup>–1</sup> retained at 1000 mA g<sup>–1</sup>, and long-term cycling durability with ∼95% capacity retention over 200 cycles.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c00023?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c00023</a>.SEM image; CV curves; XPS spectra; cycling and rate performance of different samples; and description of chemo-mechanical simulation (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c00023/suppl_file/ae1c00023_si_001.pdf">PDF</a>)Chemo-mechanical simulation of Li and effective stress evolutions in the blocks and on the cross sections of SiO<sub>2</sub>@Sn-10 and SiO<sub>2</sub>@Sn-1 electrodes (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c00023/suppl_file/ae1c00023_si_002.avi">AVI</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels