Significantly Improve Fire Safety of Silicone Rubber by Efficiently Catalyzing Ceramization on Fluorophlogopite

Yanlin Wang,Xuejun Lai,Hongqiang Li,Tian Liu,Xingrong Zeng

DOI: https://doi.org/10.1016/j.coco.2021.100683

IF: 8

2021-01-01

Composites Communications

Abstract:How to effectively improve the fire safety of silicone rubber (SR) has attracted great attention due to its wide application in our daily life. In this work, ceramifiable silicone rubber (CSR) with outstanding fire safety was prepared by incorporating fluorophlogopite (FP), Karstedt's catalyst (Pt) and gamma-aminopropyltriethoxysilane (AS) into SR. It was found that the limiting oxygen index of the Pt/AS/FP/SR composite increased to 37.5% from 27.5%, and the vertical burning test reached a UL-94 V-0 rating by adding 40 phr FP, 0.5 ph Pt and 2 phr AS. After being treated at 1000 degrees C for 1 h, the flexural strength of the composite was as high as 14.4 MPa. Meanwhile, Pt/AS/FP/SR had good mechanical properties. The mechanism revealed that the cross-link reaction of SR chains on the FP surface was efficiently promoted by the synergism of FP and Pt/AS at high temperature. The crosslinked structure further converted to amorphous Si-O-C ceramic and formed a more compact and tough residue, endowing Pt/AS/FP/SR with prominent fire safety. Our work provided a new strategy for manufacturing high-performance CSR, which showed a practical application in wires and cables with high fire safety.