Structure Effects on Swelling Properties of Hydrogels Based on Sodium Alginate and Acrylic Polymers

Grzegorz Kowalski,Mariusz Witczak,Łukasz Kuterasiński

DOI: https://doi.org/10.3390/molecules29091937

IF: 4.6

2024-04-24

Molecules

Abstract:Hydrogels based on sodium alginate (SA) and partially neutralised poly(acrylic acid) were obtained by radical polymerisation. The hydrogels were cross-linked with N,N′-methylenebisacrylamide (MBA), simultaneously grafting the resulting polymer onto SA. The findings of the FTIR spectroscopy showed that all of the hydrogels were effectively synthesized and sodium alginate was chemically bonded with the poly(sodium acrylate) matrix. DSC analysis of the melting heat and glass transition parameters indicated that the hydrogel structure had changed as a result of the cross-linking process. Sodium alginate and MBA were tested at different concentrations to determine how they affected the hydrogel properties. A very high content of the biopolymer, i.e., sodium alginate, was used in our research, up to 33 wt%. This resulted in durable and stable hydrogels with a very high ability to uptake water, comparable to hydrogels based on synthetic polymers only. The ability to swell is inversely proportional to the quantity of MBA present. By increasing the amount of sodium alginate in the hydrogel, the ability of the hydrogel to absorb water is reduced. However, water uptake remains relatively high at 350 g·g−1, even for the hydrogel with the highest SA content.

chemistry, multidisciplinary,biochemistry & molecular biology

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to study the water - absorption properties of hydrogels based on sodium alginate (SA) and acrylic polymers under the influence of different structural factors. Specifically, the author explores how these changes affect the water - absorption capacity and structural characteristics of hydrogels by changing the concentrations of the cross - linking agent N,N′ - methylene bisacrylamide (MBA) and sodium alginate. The paper also analyzes in detail the synthesis process of hydrogels and their performance under different conditions, including swelling kinetics, swelling capacity, FTIR spectroscopy, GPC (gel permeation chromatography) and DSC (differential scanning calorimetry) analysis.

### Main research questions:
1. **Influence of cross - linking agent concentration**: Study the influence of different concentrations of cross - linking agent MBA on the water - absorption capacity of hydrogels.
2. **Influence of sodium alginate content**: Study the influence of different contents of sodium alginate on the water - absorption capacity of hydrogels.
3. **Structure and properties of hydrogels**: Analyze the structure and properties of hydrogels, especially their swelling behavior and swelling kinetics, through multiple characterization techniques (such as FTIR, GPC, DSC, etc.).

### Research background:
- **Applications of hydrogels**: Hydrogels have received extensive attention due to their high water - absorption and diverse application prospects (such as in agriculture, personal care, drug delivery, etc.).
- **Advantages of natural polymers**: Compared with synthetic polymers, natural polymers (such as sodium alginate) have better biodegradability and biocompatibility, and are therefore more popular in fields such as food, agriculture and pharmaceuticals.
- **Characteristics of sodium alginate**: Sodium alginate is a natural polysaccharide with good biocompatibility and non - toxicity, and is often used to prepare hydrogels.

### Research methods:
- **Synthesis method**: Synthesize hydrogels through free - radical polymerization reaction, and simultaneously graft acrylic polymers onto sodium alginate.
- **Characterization techniques**: Use multiple techniques such as FTIR, GPC, DSC to characterize hydrogels in order to analyze their structure and properties.

### Key findings:
- **Influence of cross - linking agent**: As the concentration of MBA increases, the water - absorption capacity of hydrogels decreases because the increase in cross - linking degree leads to a more compact network structure of hydrogels.
- **Influence of sodium alginate**: As the content of sodium alginate increases, the water - absorption capacity of hydrogels also decreases, but still maintains a relatively high water - absorption rate (up to 350 g/g at most).
- **Swelling kinetics**: Hydrogels absorb water rapidly within the first 5 minutes, reaching 60% - 90% of the maximum water - absorption amount, and reach equilibrium within 20 - 40 minutes.

### Conclusion:
This study reveals the influence of these factors on the water - absorption properties of hydrogels by systematically changing the concentrations of cross - linking agents and sodium alginate. The research results show that by optimizing these parameters, hydrogels with high water - absorption capacity and stability can be prepared, which provides an important reference for the performance optimization of hydrogels in practical applications.