Abstract:DOI: 10.1002/aenm.201400842 approach involving fi xing HPW into a polyvinylpyrrolidone (PVP) and polyethersulfones (PES) matrix. A high proton conductivity of 0.066 S cm –1 is achieved at 60 °C with fully hydrated conditions when the HPW content is 30 wt%, which is very competitive with that of Nafi on115 under the same test conditions. Most signifi cantly, the proton conductivity of PES/PVPHPW is remarkably stable under a continuous fl ow of deionized (DI) water on both sides of the electrolyte membrane for a test period of more than 500 h. A PEMFC single cell based on the PES/PVP-HPW membrane exhibits impressive performance with a maximum power density of 618 mW cm −2 at 50 °C in H 2 /O 2 , and shows no obvious loss within 500 h. This hybrid PES/PVP-HPW holds great potential applications as a novel PEM due to the comparable performance and signifi cantly reduced cost compared to Nafi on. The synthesis and formation of the HPW self-anchored PES/PVP-HPW PEM through a one-step route was given in Scheme 1 . PVP, PES (mass ratio PVP:PES = 90:10) and HPW with desired content (e.g., 10 wt%, 20 wt%, or 30 wt%) were mixed in N , N -dimethylformamide (DMF) and stirred to form a transparent and homogeneous casting solution. This solution was cast onto a glass plate and dried at 343 K for 24 h to remove the solvent and obtain a PES/PVP-HPW. In the hybrid PEM, PVP that contains an N-heterocycle plays a key role in the formation of membrane and offers self-anchored site for HPW. The self-anchored HPW in the membrane acts as the sole proton conductor and cross-linking agent. PES was added to the membrane as a skeleton, to improve membrane formation and enhance the mechanical strength of the hybrid membrane, which could be replaced with other engineering plastics, for example, polysulfone, polyvinylidene fl uoride, or polyarylsulfone. Figure 1 a–c shows a photograph and cross-sectional scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images of the as-prepared PES/PVP-HPW. The photograph shown in Figure 1 a shows that the membrane was highly transparent and fl exible. The SEM image of the PES/PVP-HPW membrane cross-section exhibited no obvious phase separation, which indicates that these membranes were homogeneous (Figure 1 b). The energy-dispersive X-ray spectroscopy (EDS) tungsten (W) map (inset of Figure 1 b) indicates that the element W (green spots) was homogeneously dispersed in the membrane, which was further demonstrated by the TEM image of the hybrid membrane (Figure 1 c). The average HPW nanoparticle size was determined to be ca. 2.2 nm with a narrow distribution (Supporting Information Figure S1), which was about two HPW molecule size. [ 8 ] The X-ray diffraction (XRD) patterns of the hybrid membrane (see Supporting Information Figure S2) contained no characteristic diffraction peaks The development of proton exchange membranes (PEMs) with improved performance is critical for advancing electrochemical energy devices such as fuel cells and water electrolyzers. [ 1 ]

Polydopamine-coated polyimide nanofiber to anchor HPW and construct the pocket-like composite membrane with excellent proton conductivity and stability

NH2-UiO66 functionalized polyimide nanofiber to anchor HPW and fabricate high-performance sandwich-structure membrane for achieving excellent durability

Cross-Linkable Polymeric Ionic Liquid Improve Phosphoric Acid Retention and Long-Term Conductivity Stability in Polybenzimidazole Based PEMs

HT-PEMs Based on Nitrogen-Heterocycle Decorated Poly (arylene Ether Ketone) with Enhanced Proton Conductivity and Excellent Stability

Achieving Better Balance on the Mechanical Stability and Conduction Performance of Sulfonated Poly(ether Ether Ketone) Proton Exchange Membranes Through Polydopamine/polyethyleneimine Co-Modified Poly(vinylidene Fluoride) Nanofiber As Support

High-performance sandwich-structure PI/SPEEK+HPW nanofiber composite membrane with balanced proton conductivity and stability

Anchoring HPW by amino‐modified MIL‐101(Cr) to improve the properties of SPEEK in proton exchange membranes

A promising Al-CeZrO<sub>4</sub>/HPW-incorporated SPEEK composite membrane with improved proton conductivity and chemical stability for PEM fuel cells

Effects of Microstructural Functional Polyaniline Layers on SPEEK/HPW Proton Exchange Membranes

Consecutive and reliable proton transfer channels construction based on the compatible interface between nanofiber and SPEEK

Sulfonated poly(ether ether ketone)/aminopropyltriethoxysilane/phosphotungstic acid hybrid membranes with non-covalent bond: Characterization, thermal stability, and proton conductivity

A Self‐Anchored Phosphotungstic Acid Hybrid Proton Exchange Membrane Achieved Via One‐Step Synthesis

The Preparation of Metal–Organic‐Framework/Boron Phosphate Hybrid Materials for Improved Performances in Proton Exchange Membranes

Electrospinning-assisted Construction of Rapid Proton Conduction Channels in Halloysite Nanotube-Encapsulated Ionic Liquid-Embedded Sulfonated Poly(ether Ether Ketone) Proton Exchange Membranes

NH2-UiO-66 coated fibers to balance the excellent proton conduction efficiency and significant dimensional stability of proton exchange membrane

Polyoxometalate-polymer nanocomposites with multiplex proton transport channels for high-performance proton exchange membranes

Sulfonated Polyether Ether Ketone Composite Proton Exchange Membranes Incorporated with a Novel Hierarchical‐structure Hybrid Nanofiller Consisting Solid Superacid Zirconium Phosphate and CNTs

Inorganic/Organic Composite Proton Exchange Membrane Based on P2O5/SiO2,SPEEK and PVDF

An Enhanced Proton Conductivity of Proton Exchange Membranes by Constructing Proton-Conducting Nanopores Using PVP-UiO-66-NH-SO3H Nanoparticles

Sandwich-structure PI/SPEEK/PI proton exchange membrane developed for achieving the high durability on excellent proton conductivity and stability

Polydopamine-modified Sulfonated Polyhedral Oligomeric Silsesquioxane: an Appealing Nanofiller to Address the Trade-off Between Conductivity and Stabilities for Proton Exchange Membrane