Abstract:The study mainly investigates the effect of strain ratio on the multiaxial low cycle fatigue behaviour of 316L at 550 °C. The evolution of both axial and torsional stress amplitude is observed to go through three stages: cyclic hardening, softening and fracture. What's different is that the torsional loading experiences fewer cyclic hardening cycles compared to the axial loading. Regarding the interaction between axial and torsional stresses, it is observed that as the torsional strain increases, the axial deformation response presents a lower peak stress and a higher softening rate, while the torsional peak stress and softening rate hardly changes with the increase of axial strain amplitude. The fracture pattern is obtained through three-dimensional (3D) depth-of-field observation. It is discovered that as the strain ratio increases, the fracture pattern transits from tensile failure mode to shear failure mode. Furthermore, the orientation angle of the fracture surface increases and lies between the critical plane angle of maximum shear strain and maximum normal strain, indicating a mixed failure mode. Additionally, a comparison of nine representative critical plane models reveals that the energy-based models can better predict the multiaxial fatigue life influenced by the strain ratio. Finally, based on the analysis of deformation and failure mechanisms, a normal damage parameter weakening factor (NDWF) is introduced into the KBM-R model, and an improved normal stress component (INSC) is introduced into the Wu-R model. The two modified models well capture the impact of strain ratio and accurately predict the multiaxial fatigue life of both 316L and P92 steel.

Multiaxial Fatigue Assessment of S355 Steel in the High-Cycle Region by Using Susmel’s Criterion

Evaluation of Multiaxial High-Cycle Fatigue Criteria under Proportional Loading for S355 Steel

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

Evaluation and Comparison of Critical Plane Criteria for Multiaxial Fatigue Analysis of Ductile and Brittle Materials

Multiaxial high-cycle fatigue failure and life prediction based on critical plane method

Selection Methodology of High-Cycle Fatigue Analysis Approach for Damage Estimation in Welded Structural Joints

Multiaxial Fatigue Life Evaluation Using Strain Energy -Based Critical Plane Approach

Component Structural Equivalent Research Based on Different Failure Strength Criterions and the Theory of Critical Distance

Determination of Detail Fatigue Rating of structure under Multiaxial Loading

A Study on the Criteria of Multiaxial Fatigue for Aluminium Structures

Fatigue analysis for the aluminum alloy 7050-T7451 performed by a two scale continuum damage mechanics model

The strain ratio-dependent multiaxial low cycle fatigue behaviour and life prediction of 316L stainless steel based on critical plane at elevated temperature

A New Critical Plane Multiaxial Fatigue Criterion with an Exponent to Account for High Mean Stress Effect

Effective Fatigue Stress and Criterion for High-Cycle Multi-axial Fatigue

Static Axial Tension or Compression Stress Effects on Shear Cracks Initiating under Cyclic Torsion Loads in Multiaxial Fatigue Tests

Evaluation of finite high cycle fatigue life of hard steels using the elliptical curve method

The mean stress and phase angle effect on multiaxial fatigue behavior of a TiAl alloy: Failure analysis and life modeling

Multiaxial Fatigue Lifetime Estimation Based on New Equivalent Strain Energy Damage Model under Variable Amplitude Loading

A review of multiaxial low-cycle fatigue criteria for life prediction of metals

Load Path Sensitivity and Multiaxial Fatigue Life Prediction of Metals under Non-Proportional Loadings

A Novel Energy-Critical Multiaxial Fatigue Life Prediction for Low Cycle Fatigue under Mixed-Mode Loading