Superconducting Phase Diagrams of S-doped 2h−tase2 under Hydrostatic Pressure

Shuxiang Xu,Ziyi Liu,Pengtao Yang,Keyu Chen,Jianping Sun,Jianhong Dai,Yunyu Yin,Fang Hong,Xiaohui Yu,Mianqi Xue,Jun Gouchi,Yoshiya Uwatoko,Bosen Wang,Jinguang Cheng

DOI: https://doi.org/10.1103/physrevb.102.184511

2020-01-01

Abstract:We report the hydrostatic pressure effect on the charge density wave (CDW) and superconductivity (SC) of single-crystal 2H-TaSe2-xSx by measuring the electrical resistivity and ac magnetic susceptibility under various pressures up to 12.5 GPa. Different from the previously reported phase diagrams of CDW and SC as a function of the Se/S substitution and/or the uniaxial pressure, the superconducting transition temperature (T-c) was found to increase monotonously with increasing the pressure at first and then reaches a maximum constant above a critical pressure P-c. The maximal T-c(max) is nearly two times higher than the optimal ones via the S doping and decreases with further increasing the S-doping level. High-pressure ac magnetic susceptibility demonstrates that the superconducting volume quickly increases along with the gradual suppression of CDW and reaches nearly 1 above P-c, which provides clear evidences for pressure-induced crossover from CDW to bulk SC. High-pressure x-ray diffraction proves that there is no structural phase transition in 2H-TaSe2 up to 20 GPa; although the dependence of T-c on the volume shows distinct behaviors at the initial S doping and the applied physical pressure, they both collapse into a universal curve upon the further volume shrinkage. This indicates that both physical pressure and the S-doping-induced chemical pressure can melt CDW and enhance SC through lattice contraction consistently. In comparison with the effects of hydrostatic pressure, the S doping can destruct the CDW ground state faster due to the presence of chemical disorders, which also restrict the further enhancement of T-c after the collapse of CDW.