Abstract:To afford an intact double network (sample abbr.: DN) hydrogel, two-step crosslinking reactions of poly(2-acrylamido-2-methylpropanesulfonic acid) (i.e., PAMPS first network) and then poly(acrylic acid) (i.e., PAA second network) were conducted both in the presence of crosslinker (N,N′-methylenebisacrylamide (MBAA)). Similar to the two-step processes, different contents of 2,2,6,6-tetramethyl-1-piperidinyloxy (TEMPO) oxidized cellulose nanofibers (TOCN: 1, 2, and 3 wt.%) were initially dispersed in the first network solutions and then crosslinked. The TOCN-containing PAMPS first networks subsequently soaked in AA and crosslinker and conducted the second network crosslinking reactions (TOCN was then abbreviated as T for DN samples). As the third step, various (T–)DN hydrogels were then treated with different concentrations of FeCl3(aq) solutions (5, 50, 100, and 200 mM). Through incorporations of ferric ions into (T–)DN hydrogels, notably, three purposes are targeted: (i) strengthen the (T–)DN hydrogels through ionic bonding, (ii) significantly render ionic conductivity of hydrogels, and (iii) serve as a catalyst for the forth step to proceed with in situ chemical oxidative polymerizations of pyrroles to afford polypyrrole-containing (sample abbr.: Py) hydrogels [i.e., (T–)Py–DN samples]. The characteristic functional groups of PAMPS, PAA, and Py were confirmed by FT–IR. Uniform microstructures were observed by cryo scanning electron microscopy (cryo-SEM). These results indicated that homogeneous composites of T–Py–DN hydrogels were obtained through the four-step process. All dry samples showed similar thermal degradation behaviors from the thermogravimetric analysis (TGA). The T2–Py5–DN sample (i.e., containing 2 wt.% TOCN with 5 mM FeCl3(aq) treatment) showed the best tensile strength and strain at breaking properties (i.e., σTb = 450 kPa and εTb = 106%). With the same compositions, a high conductivity of 3.34 × 10−3 S/cm was acquired. The tough T2–Py5–DN hydrogel displayed good conductive reversibility during several “stretching-and-releasing” cycles of 50–100–0%, demonstrating a promising candidate for bioelectronic or biomaterial applications.

Facile Preparation of Agar/polyvinyl Alcohol-Based Triple-Network Composite Hydrogels with Excellent Mechanical Performances

Dual Ionically Cross-linked Double-Network Hydrogels with High Strength, Toughness, Swelling Resistance, and Improved 3D Printing Processability

Fabrication of Double-Network Hydrogels with Universal Adhesion and Superior Extensibility and Cytocompatibility by One-Pot Method

Dually cross-linked single network poly(acrylic acid) hydrogels with superior mechanical properties and water absorbency

Multi-physically Cross-Linked Hydrogels Simultaneously with MPa Level Mechanical Strengths and High Equilibrium Water Content above 70 %

Ultrastiff, Tough, and Healable Ionic-Hydrogen Bond Cross-Linked Hydrogels and Their Uses As Building Blocks to Construct Complex Hydrogel Structures

The preparation of double network hydrogel with high mechanical properties by photopolymerization under the green LED irradiation and enhancement of wet adhesion by tannic acid

Tough Supramolecular Hydrogels with Excellent Self-Recovery Behavior Mediated by Metal-Coordination Interaction

Preparation of Hierachically Crosslinked Poly(acrylamide) Hydrogels by Assistance of Crystallization of Poly(vinyl alcohol)

Chitosan/polyvinyl alcohol/tannic acid multiple network composite hydrogel: preparation and characterization

How Can Multi-Bond Network Hydrogels Dissipate Energy More Effectively: an Investigation on the Relationship Between Network Structure and Properties

Homogeneous and Real Super Tough Multi-Bond Network Hydrogels Created Through a Controllable Metal Ion Permeation Strategy

Facile fabrication of tough and biocompatible hydrogels from polyvinyl alcohol and agarose

Strengthening Network of Polyacrylic Acid/Silica Nanocomposite Hydrogels

High-strength and tough composite hydrogels reinforced by the synergistic effect of nano-doping and triple-network structures

Enhancement of Mechanical Properties of Benign Polyvinyl Alcohol/Agar Hydrogel by Crosslinking Tannic Acid and Applying Multiple Freeze/Thaw Cycles

Preparations of Tough and Conductive PAMPS/PAA Double Network Hydrogels Containing Cellulose Nanofibers and Polypyrroles

One-pot preparation of ultrastrong double network hydrogels

A robust low-friction triple network hydrogel based on multiple synergistic enhancement mechanisms

Phase Transition Temperature Controllable Poly(acrylamide- Co -Acrylic Acid) Nanocomposite Physical Hydrogels with High Strength

Facile preparation of highly adhesive yet ultra-strong poly (vinyl alcohol)/cellulose nanocrystals composite hydrogel enabled by multiple networks structure