Effects of multifunctional acrylates and thiols on the morphology and electro-optical properties of polymer-dispersed liquid crystal films

Mohsin Hassan Saeed,Yanzi Gao,Le Zhou,Tingjun Zhong,Shuaifeng Zhang,Chenyue Li,Lanying Zhang,Huai Yang

DOI: https://doi.org/10.1080/02678292.2021.1878564

2021-01-01

Liquid Crystals

Abstract:In the present paper, influence of the functionality of thiol monomers and acrylate crosslinkers, as well as crosslinker chain length on the polymer morphologies and electro-optical properties of the PDLC films, were systematically investigated. Results revealed that increasing the functionality of thiol monomers, both threshold voltage (V-th) and saturation voltage (V-sat) were increased due to the dense microstructures resulting from higher reactivity of thiol monomers. However, with increasing the functionality of acrylate monomers, V-th was increased evidently, but a relatively small rise of V-sat was found with moderate functionality monomer. Additionally, the increase in the chain length of flexible crosslinker resulted in an increase in the average size of LC droplets with a corresponding decrease in V-th and V-sat. On the whole, polymer morphology and electro-optical properties of the PDLC films can be artificially manipulated by adjusting the molecular structure of polymer matrix. A PDLC film exhibiting low driving voltage (24.0 V), moderately high contrast ratio (97.0) and fast response time (<8.0 ms), was found by employing the Pentaerythritol tetrakis (2-mercaptoacetate) (4SH), trimethylolpropane triacrylate (TMPTA) and polyethylene glycol diacrylate (PEGD 600).