Abstract:Nickel nitrides are considered to be promising for hybrid supercapacitors (HSCs) as electrochemical energy storage materials, owing to their good electrical conductivity. However, nickel nitride is prone to agglomeration in high-temperature preparation process, resulting in lower specific surface area and higher porosity, further inhibiting its energy storage performance in HSCs. Consequently, a three-dimensional Ni3N mesh with a mesoporous structure (3D Ni3N Mesh) was constructed as the electrode material for HSCs via a facile hydrothermal reaction and nitrogenization treatment in this work. The as-prepared 3D Ni3N Mesh was built from Ni3N nanoparticles as the bricks that employed the nickel hydroxide nanowires as the precursors. The electrochemical tests demonstrated that the specific capacity of the as-prepared 3D Ni3N mesh could reach 254.2 mAh g−1 at 1 A g−1 in the three-electrode cell. The specific capacity of the 3D Ni3N mesh is still up to 108.3 mAh g−1, even at a high current density of 30 A g−1. The changes of the micro-nano structure, chemical composition and energy storage mechanism of the 3D Ni3N mesh electrode materials in the charge-discharge process were also analyzed and discussed. To further demonstrate its potential applications, a HSCs was also assembled with the 3D Ni3N mesh and the activated carbon (AC) as the positive and negative electrode respectively. It is worth mentioning that the specific capacity of the 3D Ni3N mesh//AC HSCs is 59.3 mAh g−1 at 0.5 A g−1, while the energy density also reaches 56.2 Wh kg−1 at a power density of 468 W kg−1. In addition, the 3D Ni3N Mesh//AC HSCs still maintains 77.4 % capacity along with an average coulombic efficiency of 98.7 % after 5000 continuous cycles, demonstrating good cyclic reversibility.

Enhanced energy storage performance of the three-dimensional nickel nitride mesh with mesoporous structure derived from nickel hydroxide nanowires for advanced hybrid supercapacitors

Construction of Mof-Derived Ni-Co-Se/Mxene Heterostructured Composite As Hybrid Supercapacitor Cathode

Ni nanoparticles@Ni-Mo nitride nanorod arrays: a novel 3D-network hierarchical structure for high areal capacitance hybrid supercapacitors.

Boosted Electrochemical Performance of Honeycomb-Like NiCu-LDH Nanosheets Anchoring on NiCo<sub>2</sub>S<sub>4</sub> Nanotube Arrays for Flexible Solid-State Hybrid Supercapacitors

A High-Performance Hybrid Supercapacitor with NiO Derived NiO@Ni-MOF Composite Electrodes

Free-standing 3D core-shell architecture of Ni3S2@NiCoP as an efficient cathode material for hybrid supercapacitors

High-mass-loading Cobalt Iron Phosphide@nickel Vanadium Layered Double Hydroxide Heterogeneous Nanosheet Arrays for Hybrid Supercapacitors

Constructing nickel sulfide @ nickel boride hybrid nanosheet arrays with crystalline/amorphous interfaces for supercapacitors.

Hierarchical nickel hydroxide hydrate assembled by ultrathin nanosheets for high-performance hybrid supercapacitors

Designing a high-performance electrode material for hybrid supercapacitor: 1D–2D NiCo carbonate hydroxide nanofiber interlinked microsheet architecture

Hydrazine Hydrate Induced Three-Dimensional Interconnected Porous Flower-like 3D-NiCo-SDBS-LDH Microspheres for High-Performance Supercapacitor

Hydrothermal synthesis of MWCNT/Ni-Mn-S composite derived from bimetallic MOF for high-performance electrochemical energy storage

Amorphous P-NiCoS@C Nanoparticles Derived from P-doped NiCo-MOF As Electrode Materials for High-Performance Hybrid Supercapacitors

Self-assembling NiCo2S4 nanorods arrays and T-Nb2O5 nanosheets/three-dimensional nitrogen-doped garphene hybrid nanoarchitectures for advanced asymmetric supercapacitor

NiS nanoparticles assembled on biological cell walls-derived porous hollow carbon spheres as a novel battery-type electrode for hybrid supercapacitor

Facile preparation of Ni@C/hierarchically porous carbon nanocomposites with excellent electrochemical performance from Ni-MOF/porous polymers

Constructing Ni–Co PBA derived 3D/1D/2D NiO/NiCo2O4/NiMn-LDH hierarchical heterostructures for ultrahigh rate capability in hybrid supercapacitors

Rational design of three-dimensional branched NiCo-P@CoNiMo-P core/shell nanowire heterostructures for high-performance hybrid supercapacitor

Simple electrodeposition of 3D NiCoFe-layered double hydroxide nanosheet assembled nanospheres/nanoflowers on carbon cloth for high performance hybrid supercapacitors

Architecture of interconnected cubic NiCo 2 S 4 decorated mesoporous carbon with self-doped nitrogen based-hydrogel for high performance hybrid supercapacitor

Hierarchical core–shell-structured bimetallic nickel–cobalt phosphide nanoarrays coated with nickel sulfide for high-performance hybrid supercapacitors