Preparation of Cu2Y2O5 by Sol-Gel Method and Its Photocatalytic Activity
Rong Chen,Peisong Tang,Wei Yong,Huize Xu,Shiyu Wen,Wenting Tu,Qiuxuan Li,Jing Zhang,Linyu Zhu
DOI: https://doi.org/10.1080/10584587.2024.2325882
2024-10-29
Integrated Ferroelectrics
Abstract:Using citric acid (C 6 H 8 O 7 ·H 2 O), ethylene glycol (C 2 H 6 O 2 ), Yttrium(III) nitrate (Y(NO 3 ) 3 ·6H 2 O) and Copper(II) nitrate (Cu(NO 3 ) 2 ·3H 2 O) as main raw materials, the Cu 2 Y 2 O 5 samples were successfully prepared by sol-gel method.The samples were characterized by thermogravimetry differential scanning calorimetry (TG-DSC), X-ray diffraction (XRD), scanning electron microscope (SEM) and Fourier transform infrared spectroscopy (FT-IR). Using azo dye methyl orange solution as raw material to simulate wastewater, the photocatalytic activity of Cu 2 Y 2 O 5 samples was investigated under different synthesis temperatures and light conditions. The experimental results show that pure Cu 2 Y 2 O 5 samples can be prepared at a calcination temperature of 750 °C to 1000 °C, with Cu 2 Y 2 O 5 samples prepared at 800 °C having the best photocatalytic activity, with an average grain size of 0.5-1 μm. Under the UV light condition, when the light time is 45 min, the initial concentration of methyl orange is 100 mg/L, the degradation rate of Cu 2 Y 2 O 5 sample prepared at 800 °C to methyl orange reaches about 100%. Cu 2 Y 2 O 5 is a catalyst with excellent photocatalytic performance and broad application prospects.
engineering, electrical & electronic,physics, condensed matter, applied