Abstract:In this paper, the transition metals Fe and Mn are doped on the surface of rare earth concentrates by the impregnation method to prepare NH3-SCR catalyst active powder. SEM, XRD, BET, XPS, H2-TPR, NH3-TPD, NO-TPD, FTIR and other characterization methods are used to explore the surface properties and mechanism of rare earth concentrates doped with transition metals, and at the same time determine its catalysis in a simulated flue gas device performance. The results showed that the NOx conversion rate of Fe and Mn doped rare earth concentrates reached 94.8% at 200 °C. The specific surface area of the rare earth concentrate increases after Fe and Mn are doped. Fe and Mn are uniformly dispersed on the surface of the rare earth concentrate. The combined effect of Fe, Mn and the rare earth concentrate provides more weak acid sites for the reaction and promotes desorption of NO in the low temperature section. The redox performance of rare earth concentrates has also been greatly improved. Rare earth concentrates doped with Fe and Mn mainly follow the L-H mechanism in the low temperature section, and mainly follow the E-R mechanism in the high temperature section. In general, the introduction of transition metals Fe and Mn effectively improves the NH3-SCR catalytic activity of rare earth concentrates, and the rare earth concentrates themselves have good resistance and tolerance, which is useful for preparing NH3-SCR catalysts from natural minerals. It has important theoretical significance and practical value, and at the same time has a pioneering role in the application of Baiyun Obo rare earth minerals in industrial production.

Influence of rare earth elements on the structure and catalytic activity of Cu MCM41

Influence of preparation conditions of Cu-MCM41 on the synthesis of dimethyl carbonate by catalytic oxidation dimethoxymethane

Effects of Heavy Rare Earth Addition on Properties of Kl Zeolite-Supported Platinum Reforming Catalyst

Catalytic Combustion of VOCs on Pt/CuMnCe and Pt/CeY Honeycomb Monolithic Catalysts

Effect of rare earth composition on the electrochemical properties of multicomponent RENi5-xMx (M = Co, Mn, Ti) alloys

Influence of cerium precursors on the structure and reducibility of mesoporous CuO-CeO2 catalysts for CO oxidation

One-pot Synthesis of Rare Earth Modified Cu/SAPO-34 for Enhanced Selective Catalytic Reduction Denitration Performance

Synthesis of Ln-Doped Mcm-41 Mesoporous Materials and Their Catalytic Performance in Oxidation of Styrene

The Selective Catalytic Reduction Activity of Cu/MCM-41 Catalysts Prepared by Using the Cu2+–MCM-41 Mesoporous Materials with Copper Ions in the Framework As Precursors

Study on NH3-SCR performance and mechanism of Fe/Mn modified rare earth concentrate

Effects of Rare Earth Oxide on the Nucleation of Carbide Particles in Laser Cladded MMCp Coating

Effect of MnO(x) Modification on the Activity and Adsorption of CuO/Ce(0.67)Zr(0.33)O(2) Catalyst for NO Reduction.

Direct synthesis of Cu-modified MCM-41 functional materials

Synthesis, Characterization and Catalytic Application of SBA-15 Immobilized Rare Earth Metal Sandwiched Polyoxometalates

Preparation, Structure and Catalytic Performances of Rare Earth Catalytic Materials

Effect of Precipitation Method and Ce Doping on the Catalytic Activity of Copper Manganese Oxide Catalysts for CO Oxidation

The Effect of Rare Earth Modification on Ceria–zirconia Solid Solution and Its Application in Pd-only Three-Way Catalyst

Diverse Effects of Ferromagnetic-Paramagnetic Phase Transition on the Activity and Selectivity of Ferromagnetic Catalysts

EFFECT OF CALCINATION TEMPERATURE ON THE STRUCTURE AND CATALYTIC PERFORMANCE OF THE CU-MCM-41 CATALYSTS FOR THE SYNTHESIS OF DIMETHYL CARBONATE

New Insight into the Doping Effect of Transition Metals (fe, Ti, Mn, and Ce) on the Structure and Catalytic Performance of Cu-SSZ-13 Zeolite Catalysts for the NH3-SCR Reaction

Surface structure and catalytic properties of MoO3/CeO2 and CuO/MoO3/CeO2.